PA66 RFL4036 WT9-529 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Lighting applications,Electrical appliances,sporting goods,Automotive sector
High mobility,Low friction coefficient,Thermal stability,Filler: Glass fiber reinf,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/RFL4036 WT9-529 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 8.50 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.50 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.5 kJ/m² |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RFL4036 WT9-529 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 244 °C |
| 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 260 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 249 °C | |
| 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 258 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL4036 WT9-529 |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/5 | 2.8 % |
| tensile strength | 断裂 | ISO 527-2/5 | 158 Mpa |
| Tensile modulus | ASTM D638 | 11700 Mpa | |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 233 Mpa |
| elongation | 断裂 | ASTM D638 | 2.8 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 9260 Mpa |
| tensile strength | 屈服 | ASTM D638 | 160 Mpa |
| bending strength | ISO 178 | 219 Mpa | |
| Wear factor | Ring | ASTM D3702Modified | 0.250 10^-10in^5-min/ft-lb-hr |
| tensile strength | 屈服 | ISO 527-2/5 | 168 Mpa |
| Wear factor | Washer | ASTM D3702Modified | 5.00 10^-10in^5-min/ft-lb-hr |
| coefficient of friction | Static | ASTM D3702Modified | 0.61 |
| Tensile modulus | ISO 527-2/1 | 10400 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.8 % |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.67 |
| elongation | 屈服 | ASTM D638 | 2.8 % |
| tensile strength | 断裂 | ASTM D638 | 160 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 233 Mpa |
| flexural modulus | ISO 178 | 8890 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RFL4036 WT9-529 |
|---|---|---|---|
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.37 % |
| shrinkage rate | MD：24小时 | ASTM D955 | 0.40-0.60 % |
| TD：24hr | ASTM D955 | 1.0-3.0 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.58 % |