PC ELIX™ 5120 ELIX Polymers, S. L.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ 5120 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | >27 kJ/m² |
| 23°C | ISO 180/1A | >38 kJ/m² | |
| -40°C | ISO 180/1A | 30 kJ/m² |
| Mechanical properties | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ 5120 |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/50 | 50.0 MPa |
| Flexural modulus | 23°C | ISO 178 | 2320 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | 28 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2320 MPa |
| flammability | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ 5120 |
|---|---|---|---|
| burning rate | ISO 3795 | <80 mm/min | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ 5120 |
|---|---|---|---|
| density | 25°C | ISO 1183 | 1.11 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 0.65to0.75 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| Shrinkage rate | MD | ISO 2577 | 0.65to0.75 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.70 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 21.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ 5120 |
|---|---|---|---|
| vicat | ISO 306/B120 | 120 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 101 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 8.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 120 °C |