Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6T HTN52G35HSL NC010 DUPONT JAPAN
Zytel®
Fitness equipment、Electrical appliances、Car exterior decoration
High temperature resistan、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT JAPAN/HTN52G35HSL NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 38 kJ/m² |
| Electrical performance | Test Condition | Test Method | DUPONT JAPAN/HTN52G35HSL NC010 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm |
| Mechanical properties | Test Condition | Test Method | DUPONT JAPAN/HTN52G35HSL NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 11700 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.8 % |
| tensile strength | 断裂 | ISO 527-2 | 180 Mpa |
| flammability | Test Condition | Test Method | DUPONT JAPAN/HTN52G35HSL NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 25 % | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT JAPAN/HTN52G35HSL NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.20 % |
| Thermal performance | Test Condition | Test Method | DUPONT JAPAN/HTN52G35HSL NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 310 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 285 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6E-05 cm/cm/°C |