PA66 8233GHS BK102 BASF GERMANY

Ultramid®

Electrical applications,Industrial machinery

Thermal stability,High impact resistance

Plastic Datasheets

hardness	Test Condition	Test Method	BASF GERMANY/8233GHS BK102
Rockwell hardness	R-Scale	ASTM D785	121

thermal performance	Test Condition	Test Method	BASF GERMANY/8233GHS BK102
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	208 °C
		0.45MPa,Unannealed	ISO 75-2/B	215 °C
		1.8MPa,Unannealed	ISO 75-2/A	205 °C
		0.45MPa,Unannealed	ASTM D648	218 °C
Linear coefficient of thermal expansion	MD	ASTME831	3.8E-05 cm/cm/°C
Melting temperature		ASTM D3418	220 °C
Melting temperature			ISO 3146	220 °C
RTI Elec	3.0mm	UL 746	140 °C
		0.71mm	UL 746	130 °C
		1.5mm	UL 746	140 °C
RTI Imp	1.5mm	UL 746	115 °C
		3.0mm	UL 746	120 °C
		0.71mm	UL 746	115 °C
RTI Str	0.71mm	UL 746	130 °C
		3.0mm	UL 746	140 °C
		1.5mm	UL 746	140 °C

mechanical properties	Test Condition	Test Method	BASF GERMANY/8233GHS BK102
Bending modulus	23°C	ISO 178	8500 Mpa
Bending modulus		23°C	ASTM D790	8990 Mpa
bending strength	23°C	ASTM D790	280 Mpa
bending strength		23°C	ISO 178	245 Mpa
elongation	Break,80°C	ASTM D638	7.0 %
		Break,23°C	ASTM D638	3.5 %
		Break,121°C	ASTM D638	7.0 %
		Break,-40°C	ASTM D638	3.0 %
Tensile modulus	-40°C	ISO 527-2	10300 Mpa
		120°C	ISO 527-2	4010 Mpa
		23°C	ISO 527-2	10200 Mpa
		150°C	ISO 527-2	3560 Mpa
		80°C	ISO 527-2	4820 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0 %
tensile strength	Break,23°C	ISO 527-2	170 Mpa
		Break,80°C	ASTM D638	90.0 Mpa
		Break,120°C	ISO 527-2	70.0 Mpa
		Break,23°C	ASTM D638	180 Mpa
		Break,-40°C	ISO 527-2	230 Mpa
		Break,150°C	ISO 527-2	60.0 Mpa
		Break,-40°C	ASTM D638	230 Mpa
		Break,80°C	ISO 527-2	90.0 Mpa
		Break,121°C	ASTM D638	70.0 Mpa

Physical properties	Test Condition	Test Method	BASF GERMANY/8233GHS BK102
Shrinkage rate	MD：3.18mm		0.30 %
Water absorption rate	Saturation	ASTM D570	6.4 %
		Equilibrium,23°C,50%RH	ISO 62	1.8 %
		Equilibrium,50%RH	ASTM D570	1.8 %
		Saturation,23°C	ISO 62	6.4 %
		24hr	ASTM D570	1.1 %
		23°C,24hr	ISO 62	1.1 %

impact performance	Test Condition	Test Method	BASF GERMANY/8233GHS BK102
Dart impact	23°C	Internal Method	4.07 J
Impact strength of simply supported beam without notch	23°C	ISO 179	65 kJ/m²

flammability	Test Condition	Test Method	BASF GERMANY/8233GHS BK102
UL flame retardant rating	3.0mm	UL 94	HB
		1.5mm	UL 94	HB
		0.60mm	UL 94	HB