PAI T4203 (EXTRUSION) Mitsubishi Chemical Advanced Materials
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/T4203 (EXTRUSION) |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256A | 110 J/m |
| hardness | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/T4203 (EXTRUSION) |
|---|---|---|---|
| Rockwell hardness | E计秤 | ASTM D785 | 80 |
| M级 | ASTM D785 | 120 |
| Supplementary Information | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/T4203 (EXTRUSION) |
|---|---|---|---|
| limiting pv value | 内部方法 | 0.140 MPa·m/s |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/T4203 (EXTRUSION) |
|---|---|---|---|
| dielectric strength | ASTM D149 | 23 kV/mm | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.026 |
| Surface Resistivity | 内部方法 | >1.0E+16 ohms | |
| dielectric constant | 1MHz | ASTM D150 | 4.20 |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/T4203 (EXTRUSION) |
|---|---|---|---|
| tensile strength | 极限 | ASTM D638 | 138 MPa |
| elongation | 断裂 | ASTM D638 | 10 % |
| compressive strength | 10%应变 | ASTM D695 | 165 MPa |
| bending strength | 屈服 | ASTM D790 | 165 MPa |
| Tensile modulus | ASTM D638 | 4140 MPa | |
| Flexural modulus | ASTM D790 | 4140 MPa | |
| Compression Modulus | ASTM D695 | 3300 MPa | |
| Wear factor | ASTM D3702 | >2000 10^-8mm³/N·m | |
| shear strength | ASTM D732 | 110 MPa | |
| coefficient of friction | 与钢-静态 | 内部方法 | 0.35 |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/T4203 (EXTRUSION) |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/T4203 (EXTRUSION) |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 1.7 % |
| 24hr | ASTM D570 | 0.40 % | |
| density | ASTM D792 | 1.41 g/cm³ |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/T4203 (EXTRUSION) |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 278 °C |
| Linear coefficient of thermal expansion | MD2：-40到149°C | ASTME831 | 3.1E-05 cm/cm/°C |
| Maximum operating temperature LongTerm, Air | 260 °C | ||
| Glass Transition Temperature | ASTM D3418 | 275 °C | |
| thermal conductivity | ASTMF433 | 0.26 W/m/K |