Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1803R SABIC INNOVATIVE SHANGHAI
SABIC®
Automotive sector、Laptop case、Electronic field、Electrical field
high viscosity、High temperature resistan、enhance、Thermal stability、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/1803R |
|---|---|---|---|
| -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1A | 70 kJ/m² | |
| ASTMD4812 | 无断裂 | ||
| ASTM D256 | 700 J/m | ||
| -30°C | ISO 180/1A | 12 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/1803R |
|---|---|---|---|
| Hardness (Rockwell R) | ASTM D785 | 120 | |
| ISO 2039-2 | 120 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/1803R |
|---|---|---|---|
| fracture | ISO 527-2/50 | >70 % | |
| --2 | ASTM D638 | 2350 Mpa | |
| yield | ASTM D638 | 63.0 Mpa | |
| ASTM D638 | 6.0 % | ||
| fracture | ASTM D638 | >70 % | |
| yield | ISO 527-2/50 | 63.0 Mpa | |
| ISO 527-2/50 | 6.0 % | ||
| Yield, 50.0mm span | ASTM D790 | 90.0 Mpa | |
| --8 | ISO 178 | 90.0 Mpa | |
| 50.0mm span | ASTM D790 | 2300 Mpa | |
| --7 | ISO 178 | 2300 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/1803R |
|---|---|---|---|
| Volume resistivity | ASTMD257 | >1.0E+15 ohms·cm | |
| dielectric constant | 1MHz | ASTMD150 | 3.00 |
| Dissipation Factor | 60Hz | ASTMD150 | 1E-03 |
| dielectric strength | 1.60mm | ASTM D2863 | 27 KV/mm |
| Dissipation Factor | 1MHz | ASTMD150 | 0.010 |
| dielectric constant | 60Hz | ASTMD150 | 3.00 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/1803R |
|---|---|---|---|
| refractive index | ASTMD542 | 1.586 | |
| Haze ratio | 2540µm | ASTM D1003 | <0.80 % |
| transmissivity | 2540µm | ASTM D1003 | 88.0to90.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/1803R |
|---|---|---|---|
| UL flame retardant rating | 1.60mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/1803R |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Balance, 23 ° C | ASTM D570 | 0.35 % | |
| density | ASTMD792 | 1.20 g/cm³ | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 17.0 cm3/10min |
| Shrinkage rate | MD：--1 | 内部方法 | 0.50-0.70 % |
| Saturation, 23 ° C | ISO 62 | 0.35 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/1803R |
|---|---|---|---|
| 23 to 80 ° C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| thermal conductivity | DENKA Method | 0.20 W/m/K | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| -40 to 95 ° C | ASTME831 | 7E-05 cm/cm/°C |