PEI ProPolymers PEI 2200 美国ProPolymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 美国ProPolymers/ProPolymers PEI 2200 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 480 J/m | |
| ASTM D256 | 30.0 kJ/m² | ||
| Impact strength of cantilever beam gap | ASTM D256 | 9.00 kJ/m² | |
| ASTM D256 | 64 J/m |
| hardness | Test Condition | Test Method | 美国ProPolymers/ProPolymers PEI 2200 |
|---|---|---|---|
| Rockwell hardness | M级 | 114 |
| Mechanical properties | Test Condition | Test Method | 美国ProPolymers/ProPolymers PEI 2200 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 4.0 % |
| Flexural modulus | ASTM D790 | 6890 MPa | |
| tensile strength | 屈服 | ASTM D638 | 131 MPa |
| bending strength | ASTM D790 | 228 MPa |
| physical property | Test Condition | Test Method | 美国ProPolymers/ProPolymers PEI 2200 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30to0.50 % |
| Water absorption rate | 24hr | ASTM D570 | 0.19 % |
| density | ASTM D792 | 1.42 g/cm³ | |
| Shrinkage rate | TD | ASTM D955 | 0.40to0.60 % |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 6.0 g/10min |
| Thermal performance | Test Condition | Test Method | 美国ProPolymers/ProPolymers PEI 2200 |
|---|---|---|---|
| vicat | ASTM D1525 | 221 °C | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ASTM D648 | 210 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 210 °C |