Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 1013G10 MITSUBISHI ENGINEERING JAPAN
Novamid®
Electronic and Electrical
heat-resisting、Aging resistance、Fiber optic reinforcement、Heat aging
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G10 |
|---|---|---|---|
| Heat distortion temperature | HDT | D648 | 189(215) °C |
| Impact strength of cantilever beam gap | ISO 179 | 32(127) KJ/m | |
| Breaking stress | 100(60) Mpa | ||
| Tensile modulus | ISO 527-1 | 5000(2200) Mpa | |
| bending strength | D178 | 172(87) Mpa | |
| Flexural modulus | D178 | 4500(2200) Mpa | |
| elongation | 断裂 | 2.3(12.5) % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G10 |
|---|---|---|---|
| dielectric strength | IEC 243-1 | 25 MV/m | |
| dielectric constant | ASTM D 790 | 4 Pf/m | |
| Dielectric loss | IEC 250 | 0.012(0.022) | |
| Compared to the Leakage Traceability Index (CTI) | IEC 112 | 375 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G10 |
|---|---|---|---|
| Shrinkage rate | 0.4 MD% | ||
| 1.3 TD% | |||
| Water absorption rate | D570 | 3.1 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1013G10 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |