ABS VW800 UMG JAPAN
UMG ABS®
--
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | UMG JAPAN/VW800 |
---|---|---|---|
Rockwell hardness | R计秤,23°C | ISO 2039-2 | 103 |
Mechanical properties | Test Condition | Test Method | UMG JAPAN/VW800 |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 13 kg·cm/cm(J/M)ft·lb/in | |
bending strength | ASTM D790/ISO 178 | 68 kg/cm²(MPa)[Lb/in²] | |
Flexural modulus | ASTM D790/ISO 178 | 2500 kg/cm²(MPa)[Lb/in²] | |
bending strength | 23°C | ISO 178 | 68.0 Mpa |
Flexural modulus | 23°C | ISO 178 | 2500 Mpa |
Tensile modulus | ASTM D638/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] | |
23°C | ISO 527-2 | 2400 Mpa | |
Rockwell hardness | ASTM D785 | 103 | |
tensile strength | ASTM D638/ISO 527 | 41 kg/cm²(MPa)[Lb/in²] | |
23°C | ISO 527-2 | 41.0 Mpa |
Physical properties | Test Condition | Test Method | UMG JAPAN/VW800 |
---|---|---|---|
Shrinkage rate | ASTM D955 | 0.7-0.8 % | |
density | ASTM D792/ISO 1183 | 1.18 | |
melt mass-flow rate | ASTM D1238/ISO 1133 | 30 g/10min |
flammability | Test Condition | Test Method | UMG JAPAN/VW800 |
---|---|---|---|
UL flame retardant rating | 2.0mm | UL 94 | 5VB |
1.5mm | UL 94 | V-0 |
physical property | Test Condition | Test Method | UMG JAPAN/VW800 |
---|---|---|---|
Shrinkage rate | MD:23°C | ISO 294-4 | 0.50-0.70 % |
Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 30.0 cm3/10min |
Thermal performance | Test Condition | Test Method | UMG JAPAN/VW800 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 74.0 °C |
HDT | ASTM D648/ISO 75 | 74 ℃(℉) | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-05 cm/cm/°C |
ASTM D696/ISO 11359 | 8 mm/mm.℃ |