PC
PC SABIC INNOVATIVE NANSHA EXL1132 WH9E207NS
Cold resistant grade
US$ 3,311 / MT
FOB Guangzhou port, China
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1132 WH9E207NS
bending strengthISO 17885.0 Mpa
elongationBreakASTM D638110 %
Tensile modulusASTM D6382280 Mpa
bending strengthYield,50.0mmSpanASTM D79095.1 Mpa
tensile strengthBreakASTM D63858.7 Mpa
Bending modulusISO 1782240 Mpa
Tensile strainYieldISO 527-2/505.0 %
elongationYieldASTM D6385.8 %
Bending modulus50.0mmSpanASTM D7902320 Mpa
Tensile modulusISO 527-2/12150 Mpa
tensile strengthBreakISO 527-2/5055.0 Mpa
YieldISO 527-2/5057.0 Mpa
Tensile strainBreakISO 527-2/50100 %
tensile strengthYieldASTM D63858.1 Mpa
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1132 WH9E207NS
Extreme Oxygen IndexISO 4589-232 %
Hot filament ignition temperature1.0mmIEC 60695-2-13875 °C
3.0mmIEC 60695-2-13875 °C
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
1.0mmIEC 60695-2-12850 °C
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1132 WH9E207NS
Linear coefficient of thermal expansionTD：-40to40°CASTME8317.6E-05 cm/cm/°C
MD：23to80°CISO 11359-27.5E-05 cm/cm/°C
Ball Pressure Test125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27.5E-05 cm/cm/°C
RTI StrUL 746125 °C
Hot deformation temperature1.8MPa,Unannealed,100mmSpanISO 75-2/Ae125 °C
Vicat softening temperature--ISO 306/B50144 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648124 °C
Vicat softening temperatureASTM D152511144 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8317.2E-05 cm/cm/°C
RTI ElecUL 746130 °C
RTI ImpUL 746120 °C
Vicat softening temperature--ISO 306/B120145 °C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648137 °C
0.45MPa,AnnealedISO 75-2/Be136 °C
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1132 WH9E207NS
melt mass-flow rate300°C/1.2kgASTM D123817 g/10min
Shrinkage rateTD：3.20mmInternal Method0.40-0.80 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Shrinkage rateMD：3.20mmInternal Method0.40-0.80 %
Water absorption rateSaturation,23°CISO 620.35 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113316.0 cm3/10min
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1132 WH9E207NS
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Charpy Notched Impact Strength-30°CISO 179/1eA25 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A55 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Charpy Notched Impact Strength23°CISO 179/1eA60 kJ/m²
Dart impact23°C,TotalEnergyASTM D376369.6 J
Impact strength of cantilever beam gap-30°CISO 180/1A20 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL1132 WH9E207NS
Ball Pressure TestH358/30ISO 2039-195.0 Mpa