PC COVESTRO SHANGHAI FR3010 012881

US$ 3,000 / MT

FOB Shanghai port, China

flame retardant performance	Test Condition	Test Method	COVESTRO SHANGHAI/FR3010 012881
Relative temperature of heating wire	2.20mm	IEC 60695-2-13	960 °C
Ignition temperature of heating wire	3.00mm	IEC 60695-2-12	850 °C
Ignition temperature of heating wire		2.20mm	IEC 60695-2-12	850 °C
Relative temperature of heating wire	1.50mm	IEC 60695-2-13	960 °C
Ignition temperature of heating wire	1.50mm	IEC 60695-2-12	850 °C
Ignition temperature of heating wire		1.00mm	IEC 60695-2-12	850 °C
Relative temperature of heating wire	1.00mm	IEC 60695-2-13	960 °C
Relative temperature of heating wire		3.00mm	IEC 60695-2-13	960 °C
UL flame retardant rating		UL -94	V-0.5VB 3.00mm
Electrical performance	Test Condition	Test Method	COVESTRO SHANGHAI/FR3010 012881
Dissipation factor	23°C	IEC 60250	7E-03 1MHz
Dielectric constant	23°C	IEC 60250	3.1 1MHz
Volume resistivity		IEC 60093	1E+16 Ω.cm
Dissipation factor	相对漏电起痕指数	IEC 60112	350 V
Surface resistivity		IEC 60093	1E+16 Ω.cm
Dielectric strength		IEC 60243-1	35 KV/mm
mechanical properties	Test Condition	Test Method	COVESTRO SHANGHAI/FR3010 012881
tensile strength	23°C	ISO 527-2	60 Mpa
Elongation at Break	23°C	ISO 527-2	>50 %
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	35 kJ/m²
Tensile modulus	23°C	ISO 527-2	2700 Mpa
thermal performance	Test Condition	Test Method	COVESTRO SHANGHAI/FR3010 012881
Linear coefficient of thermal expansion	MD	ISO 11359-2	7.6E-05 cm/cm/°C
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	100 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	8E-05 cm/cm/°C
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	90 °C
Vicat softening temperature		ISO 306/B50	106 °C
Physical properties	Test Condition	Test Method	COVESTRO SHANGHAI/FR3010 012881
Water absorption rate	(23°C,50RH)	ISO 62	0.20 %
Shrinkage rate	MD2.0mm	ISO 294-4	0.60 %
melt mass-flow rate	240℃/5.0Kg	ISO 1133	25 cm3/10min
Water absorption rate	(23°C,24hr)	ISO 62	0.50 %
Shrinkage rate	TD2.0mm	ISO 294-4	0.60 %