PC FR3010 012881 COVESTRO SHANGHAI
Makrolon®
Medical packaging
Chemical resistance、Flame retardant、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | COVESTRO SHANGHAI/FR3010 012881 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 35 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2 | 2700 Mpa |
| elongation at break | 23°C | ISO 527-2 | >50 % |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 60 Mpa |
| Electrical performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR3010 012881 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 350 V |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| dielectric constant | 23°C | IEC 60250 | 3.1 1MHz |
| Surface Resistivity | IEC 60093 | 1E+16 Ω.cm | |
| Dissipation Factor | 23°C | IEC 60250 | 7E-03 1MHz |
| Volume resistivity | IEC 60093 | 1E+16 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR3010 012881 |
|---|---|---|---|
| Relative temperature of heating wire | 1.00mm | IEC 60695-2-13 | 960 °C |
| GWIT | 2.20mm | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | UL -94 | V-0.5VB 2.20mm | |
| Relative temperature of heating wire | 2.20mm | IEC 60695-2-13 | 960 °C |
| UL flame retardant rating | UL -94 | V-0.5VA 3.00mm | |
| UL -94 | 1.00mm | ||
| GWIT | 3.00mm | IEC 60695-2-12 | 850 °C |
| Relative temperature of heating wire | 3.00mm | IEC 60695-2-13 | 960 °C |
| GWIT | 1.00mm | IEC 60695-2-12 | 850 °C |
| Relative temperature of heating wire | 1.50mm | IEC 60695-2-13 | 960 °C |
| UL flame retardant rating | UL -94 | V-0 1.50mm | |
| UL -94 | 0.75mm | ||
| GWIT | 1.50mm | IEC 60695-2-12 | 850 °C |
| physical property | Test Condition | Test Method | COVESTRO SHANGHAI/FR3010 012881 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.50 % |
| Shrinkage rate | MD2.0mm | ISO 294-4 | 0.60 % |
| melt mass-flow rate | 240℃/5.0Kg | ISO 1133 | 25 cm3/10min |
| Water absorption rate | (23°C,50RH) | ISO 62 | 0.20 % |
| Shrinkage rate | TD2.0mm | ISO 294-4 | 0.60 % |
| Thermal performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR3010 012881 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 90 °C |
| vicat | ISO 306/B50 | 106 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7.6E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 100 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 8E-05 cm/cm/°C |