PS Stirolan AE V0 1.6 Soredi S.p.a.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Soredi S.p.a./Stirolan AE V0 1.6 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -20°C,3.20mm | ASTM D256 | 30 J/m |
| 23°C,3.20mm | ASTM D256 | 60 J/m |
| hardness | Test Condition | Test Method | Soredi S.p.a./Stirolan AE V0 1.6 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 80 |
| Mechanical properties | Test Condition | Test Method | Soredi S.p.a./Stirolan AE V0 1.6 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 40 % |
| tensile strength | 断裂 | ASTM D638 | 24.0 MPa |
| Flexural modulus | ASTM D790 | 2300 MPa | |
| bending strength | 断裂 | ASTM D790 | 40.0 MPa |
| tensile strength | 屈服 | ASTM D638 | 22.0 MPa |
| Electrical performance | Test Condition | Test Method | Soredi S.p.a./Stirolan AE V0 1.6 |
|---|---|---|---|
| relative permittivity | 1MHz | IEC 60250 | 2.40 |
| flammability | Test Condition | Test Method | Soredi S.p.a./Stirolan AE V0 1.6 |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 960 °C |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Soredi S.p.a./Stirolan AE V0 1.6 |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 10 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.40to0.60 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| density | ASTM D792 | 1.18 g/cm³ |
| Thermal performance | Test Condition | Test Method | Soredi S.p.a./Stirolan AE V0 1.6 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 80.0 °C |
| vicat | ASTM D15254 | 90.0 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 9E-05 cm/cm/°C |