Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS K/30 LATI ITALY
LATILUB
--
Filler: Carbon fiber rein、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI ITALY/K/30 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 25 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LATI ITALY/K/30 |
|---|---|---|---|
| Tensile modulus | 60°C | ISO 527-2/1 | 23500 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 0.80 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 185 Mpa |
| Tensile modulus | 90°C | ISO 527-2/1 | 21000 Mpa |
| 23°C | ISO 527-2/1 | 25000 Mpa | |
| Tensile strain | 断裂,120°C | ISO 527-2/5 | 1.6 % |
| Tensile modulus | 150°C | ISO 527-2/1 | 11000 Mpa |
| 120°C | ISO 527-2/1 | 15000 Mpa | |
| Tensile strain | 断裂,150°C | ISO 527-2/5 | 1.8 % |
| tensile strength | 断裂,90°C | ISO 527-2/5 | 130 Mpa |
| 断裂,120°C | ISO 527-2/5 | 85.0 Mpa | |
| 断裂,150°C | ISO 527-2/5 | 70.0 Mpa | |
| Tensile strain | 断裂,60°C | ISO 527-2/5 | 0.90 % |
| 断裂,90°C | ISO 527-2/5 | 1.3 % | |
| tensile strength | 断裂,60°C | ISO 527-2/5 | 165 Mpa |
| Electrical performance | Test Condition | Test Method | LATI ITALY/K/30 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+04 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1E+02 ohms |
| flammability | Test Condition | Test Method | LATI ITALY/K/30 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LATI ITALY/K/30 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.10-0.20 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.050 % |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.15-0.25 % |
| Thermal performance | Test Condition | Test Method | LATI ITALY/K/30 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 280 °C |
| vicat | ISO 306/B50 | 255 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 270 °C |
| Continuous use temperature | 225 °C | ||
| Linear coefficient of thermal expansion | MD：30到100°C | ISO 11359-2 | 2E-06 cm/cm/°C |