PC 3412ECR-OR7G005 SABIC INNOVATIVE NANSHA
LEXAN™ 
Plastic bag,Automotive External Parts,Industrial applications,Electrical appliances,Lighting applications,Medical supplies
Glass fiber reinforced,enhance,Flame retardant,High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-OR7G005
Ball Pressure Test125°CIEC 60695-10-2Pass
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648141 °C
1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af136 °C
0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf141 °C
Linear coefficient of thermal expansionMD:-40to40°CASTME8313E-05 cm/cm/°C
TD:-40to40°CASTME8317E-05 cm/cm/°C
TD:23to80°CISO 11359-27E-05 cm/cm/°C
MD:23to80°CISO 11359-23E-05 cm/cm/°C
RTI ElecUL 746130 °C
RTI ImpUL 746130 °C
RTI StrUL 746130 °C
Vicat softening temperature--ISO 306/B120146 °C
--ISO 306/B50145 °C
ASTM D152510147 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-OR7G005
Bending modulus50.0mmSpanASTM D7905000 Mpa
ISO 1785500 Mpa
bending strengthYield,50.0mmSpanASTM D790156 Mpa
ISO 178140 Mpa
elongationYieldASTM D6383.1 %
Tensile modulusASTM D6385500 Mpa
ISO 527-2/16000 Mpa
Tensile strainBreakISO 527-2/53.2 %
YieldISO 527-2/52.8 %
tensile strengthBreakISO 527-2/590.0 Mpa
YieldASTM D63890.0 Mpa
YieldISO 527-2/595.0 Mpa
BreakASTM D63887.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-OR7G005
Arc resistanceASTM D495PLC7
Compared to the anti leakage trace indexCTIUL 746PLC 3
Dissipation factor1MHzIEC 602500.010
50HzIEC 602500.020
60HzIEC 602500.020
High arc combustion indexHAIUL 746PLC 3
High voltage arc tracing rateHVTRUL 746PLC 3
Hot wire ignitionHWIUL 746PLC 0
Relative permittivity60HzIEC 602503.30
50HzIEC 602503.30
1MHzIEC 602503.30
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-OR7G005
densityISO 11831.36 g/cm³
ASTM D7921.30 g/cm³
melt mass-flow rate300°C/1.2kgASTM D12387.0 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11337.00 cm3/10min
Shrinkage rateTD:3.20mmInternal Method0.20-0.50 %
MD:3.20mmInternal Method0.20-0.50 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
Saturation,23°CISO 620.29 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-OR7G005
Charpy Notched Impact Strength23°CISO 179/1eA6.0 kJ/m²
-30°CISO 179/1eA5.0 kJ/m²
Dart impact23°C,TotalEnergyASTM D376320.0 J
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
23°CISO 180/1A7.0 kJ/m²
23°CASTM D256110 J/m
-30°CASTM D256110 J/m
Impact strength of simply supported beam without notch-30°CISO 179/1eU40 kJ/m²
23°CISO 179/1eU40 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U35 kJ/m²
-30°CISO 180/1U35 kJ/m²
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-OR7G005
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
Extreme Oxygen IndexISO 4589-240 %
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
UL flame retardant rating3.0mmUL 945VA
1.5mmUL 94V-0