Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LDPE 582E DOW USA
DOWLEX™
chip
High transparency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DOW USA/582E |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 3.5 g/10min |
| film thickness | 50 um | ||
| density | ASTM D-792 | 0.923 g/m3 |
| Mechanical properties | Test Condition | Test Method | DOW USA/582E |
|---|---|---|---|
| Tensile yield strength (MD) | 50um | ASTM D-882 | 9 Mpa |
| Elmendorf Tear Strength (MD) | 50um | ASTM D-1922 | 500 g |
| Elmendorf Tear Strength (TD) | 50um | ASTM D-1922 | 400 g |
| Tensile elongation at break (MD) | 50um | ASTM D-882 | 450 % |
| Tensile yield strength (TD) | 50um | ASTM D-882 | 9 Mpa |
| Tensile strength at break (MD) | 50um | ASTM D-882 | 17 Mpa |
| Tangent modulus (TD) | 2% Secant，50um | ASTM D-882 | 175 Mpa |
| Tensile elongation at break (TD) | 50um | ASTM D-882 | 650 % |
| ASTM D-1894 | 0.16-0.2 | ||
| Tensile fracture strength (TD) | 50um | ASTM D-882 | 15 Mpa |
| Falling hammer impact | 50um | ASTM D-1709A | 120 g |
| Tangent modulus (MD) | 2% Secant，50um | ASTM D-882 | 190 Mpa |
| optical performance | Test Condition | Test Method | DOW USA/582E |
|---|---|---|---|
| Haze ratio | 50um | ASTM D-1003 | 7 % |
| gloss | 20°，50um | ASTM D-2457 | 70 |
| processability | Test Condition | Test Method | DOW USA/582E |
|---|---|---|---|
| Melt Temperature | 150-170 °C |
| Thermal performance | Test Condition | Test Method | DOW USA/582E |
|---|---|---|---|
| vicat | ISO 306/A | 93 °C |