PC/PBT 357-1001 SABIC INNOVATIVE SHANGHAI
XENOY™ 
Electrical field,Electronic field,Architectural application field,Outdoor applications,Electrical appliances,Engine hood parts,Medical supplies,Nursing supplies,Plastic bag,Casters,Lawn equipment,Garden equipment,Household goods,Liquid handling,Petroleum Applications,Natural gas supplies,Industrial applications,Spool,Shell,switch
Impact modification
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Rockwell hardnessR-ScaleASTM D785117
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Ball Pressure Test125°CIEC 60695-10-2Pass
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D64898.0 °C
1.8MPa,Unannealed,6.40mmASTM D64899.0 °C
1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af84.0 °C
0.45MPa,Unannealed,3.20mmASTM D648135 °C
0.45MPa,Unannealed,6.40mmASTM D648138 °C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-28.4E-05 cm/cm/°C
MD：-40to40°CASTME8319.2E-05 cm/cm/°C
TD：-40to40°CASTME8318.4E-05 cm/cm/°C
MD：-40to40°CISO 11359-27.2E-05 cm/cm/°C
MD：60to138°CASTME8311.2E-04 cm/cm/°C
RTI ElecUL 746120 °C
RTI ImpUL 746120 °C
RTI StrUL 746140 °C
Vicat softening temperature--ISO 306/B120150 °C
--ISO 306/B50145 °C
ASTM D152513134 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Bending modulus50.0mmSpanASTM D7902100 Mpa
ISO 1782000 Mpa
bending strengthYield,50.0mmSpanASTM D79078.0 Mpa
ISO 17873.0 Mpa
Break,50.0mmSpanASTM D79078.0 Mpa
Tensile modulusASTM D6382020 Mpa
ISO 527-2/12200 Mpa
Tensile strainYieldASTM D6385.0 %
BreakISO 527-2/5030 %
BreakASTM D63854 %
YieldISO 527-2/505.0 %
tensile strengthYieldASTM D63848.0 Mpa
YieldISO 527-2/5050.0 Mpa
BreakISO 527-2/5040.0 Mpa
BreakASTM D63842.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Arc resistanceASTM D495PLC6
Compared to the anti leakage trace indexCTIUL 746PLC 2
Dielectric constant100HzASTM D1503.20
1MHzASTM D1503.20
Dielectric strength3.20mm,inAirASTM D14919 KV/mm
3.20mm,in OilASTM D14919 KV/mm
1.60mm,in OilASTM D14925 KV/mm
Dissipation factor100HzASTM D1503E-03
1MHzASTM D1500.030
High arc combustion indexHAIUL 746PLC 3
High voltage arc tracing rateHVTRUL 746PLC 3
Hot wire ignitionHWIUL 746PLC 2
Volume resistivityASTM D257>1.2E+16 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
densityISO 11831.34 g/cm³
ASTM D7921.35 g/cm³
melt mass-flow rate250°C/5.0kgASTM D12389.6 g/10min
Melt Volume Flow Rate (MVR)250°C/5.0kgISO 11338.00 cm3/10min
Outdoor applicabilityUL 746Cf2
Shrinkage rateTD：--2Internal Method0.90-1.3 %
MD：3.20mmInternal Method1.0-1.4 %
MD：--2Internal Method0.80-1.1 %
MD：--3Internal Method1.0-1.4 %
TD：--3Internal Method1.2-1.6 %
Specific volumeASTM D7920.740 cm³/g
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Saturation,23°CISO 620.50 %
24hrASTM D5700.080 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Charpy Notched Impact Strength23°CISO 179/1eA45 kJ/m²
Dart impact23°CASTM D302943.4 J
23°C11ASTM D302943.0 J
23°C,TotalEnergyASTM D376335.8 J
Impact strength of cantilever beam gap23°CASTM D4812NoBreak
-30°CISO 180/1A10 kJ/m²
23°CISO 180/1A45 kJ/m²
23°CASTM D256320 J/m
-30°CASTM D256150 J/m
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/357-1001
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
Extreme Oxygen IndexASTM D286330 %
Hot filament ignition temperature2.0mmIEC 60695-2-13750 °C
3.0mmIEC 60695-2-13725 °C
1.0mmIEC 60695-2-13775 °C
UL flame retardant rating0.46mmUL 94HB
3.0mmUL 945VA
0.63mmUL 94V-0