PA6 73G15HSL BK363 DUPONT USA
Zytel®
Automotive components、Industrial machinery
Thermal stability、High crystallinity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/73G15HSL BK363 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| -30°C | ISO 179/1eU | 40 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/73G15HSL BK363 |
|---|---|---|---|
| Odor | VDA270 | 4.00 | |
| Emissions of Organic Compounds | VDA277 | 8.50 µgC/g |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/73G15HSL BK363 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 40 kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | ISO 527-2 | 6500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.3 % |
| Tensile modulus | ASTM D638/ISO 527 | 6500 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 断裂 | ISO 527-2 | 130 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 6 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 2.3 % | |
| tensile strength | ASTM D638/ISO 527 | 130 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | DUPONT USA/73G15HSL BK363 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 22 KV/mm |
| other | Test Condition | Test Method | DUPONT USA/73G15HSL BK363 |
|---|---|---|---|
| characteristic | PA6.15％玻纤增强.热稳定.注射成型 |
| Physical properties | Test Condition | Test Method | DUPONT USA/73G15HSL BK363 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.25 |
| flammability | Test Condition | Test Method | DUPONT USA/73G15HSL BK363 |
|---|---|---|---|
| Fogging-G-value | condensate | ISO 6452 | 0.0 g |
| FMVSS flammability | FMVSS302 | B | |
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 21 % | |
| burning rate | 1.00mm | ISO 3795 | 25 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/73G15HSL BK363 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 7.6 % |
| ThermalConductivityofMelt | 0.20 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 2.5 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/73G15HSL BK363 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Linear coefficient of thermal expansion | MD：55to160°C | ISO 11359-2 | 1.5E-05 cm/cm/°C |
| TD：55to160°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| vicat | ISO 306/B50 | 215 °C | |
| melting temperature | ISO 11357-3 | 221 °C | |
| Linear coefficient of thermal expansion | TD：-- | ISO 11359-2 | 9E-05 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 3.5E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 7.8E-05 cm/cm/°C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 204 ℃（℉） |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1.6E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 204 °C | |
| melting temperature | 221 ℃（℉） |