PP Homopolymer TOTAL Polypropylene PPC 4170 TOTAL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | TOTAL/TOTAL Polypropylene PPC 4170 |
|---|---|---|---|
| Secant modulus | 2%正割,TD:50µm,吹塑薄膜 | ASTM D882 | 600 MPa |
| tensile strength | TD:屈服,50µm,吹塑薄膜 | ASTM D882 | 25.0 MPa |
| OTr | 23°C,0%RH,50µm,吹塑薄膜 | ASTM D3985 | 2100 cm³/m²/24hr |
| Secant modulus | 2%正割,MD:50µm,吹塑薄膜 | ASTM D882 | 690 MPa |
| Elmendorf tear strength | TD:50µm,吹塑薄膜 | ASTM D1922 | 300 g |
| elongation | MD:断裂,50µm,吹塑薄膜 | ASTM D882 | 750 % |
| Elmendorf tear strength | MD:50µm,吹塑薄膜 | ASTM D1922 | 55 g |
| tensile strength | MD:屈服,50µm,吹塑薄膜 | ASTM D882 | 26.0 MPa |
| Water Vapor Transmission Rate | 38°C,100%RH,50µm,吹塑薄膜 | ASTMF1249 | 7.0 g/m²/24hr |
| Dart impact | 50µm,吹塑薄膜 | ASTM D1709A | 350 g |
| elongation | TD:断裂,50µm,吹塑薄膜 | ASTM D882 | 770 % |
| tensile strength | TD:断裂,50µm,吹塑薄膜 | ASTM D882 | 38.0 MPa |
| film thickness | 50 µm | ||
| tensile strength | MD:断裂,50µm,吹塑薄膜 | ASTM D882 | 59.0 MPa |
| optical performance | Test Condition | Test Method | TOTAL/TOTAL Polypropylene PPC 4170 |
|---|---|---|---|
| Haze ratio | 50.0µm,吹塑薄膜 | ASTM D1003 | 72 % |
| gloss | 45°,50.0µm,吹塑薄膜 | ASTM D2457 | 7 |
| physical property | Test Condition | Test Method | TOTAL/TOTAL Polypropylene PPC 4170 |
|---|---|---|---|
| density | ASTM D1505 | 0.905 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 0.75 g/10min |
| Thermal performance | Test Condition | Test Method | TOTAL/TOTAL Polypropylene PPC 4170 |
|---|---|---|---|
| melting temperature | DSC | 160to165 °C |