PP 3720E 10000 SABIC INNOVATIVE SHANGHAI
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/3720E 10000 |
|---|---|---|---|
| melt mass-flow rate | 230℃，2.16kg | ISO 1133 | 18 g/10min |
| density | ISO 1183 | 1.04 g/cm |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/3720E 10000 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527 | 25 Mpa |
| Shore hardness | ISO 868 | 71 | |
| tensile strength | 屈服 | ISO 527 | 28 Mpa |
| Flexural modulus | ASTM D-790 | 2200 Mpa | |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 6 KJ/m |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/4A | 6 KJ/m |
| elongation | 断裂 | ISO 527 | 45 % |
| Impact strength of cantilever beam gap | -20℃ | ISO 180/4A | 3 KJ/m |
| 0℃ | ISO 180/4A | 3.5 KJ/m | |
| Impact strength of simply supported beam without notch | -40℃ | ISO 179/1eU | 18 KJ/m |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/3720E 10000 |
|---|---|---|---|
| Shrinkage rate | 24 hours after injection moulding | SABIC method | 1.1 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/3720E 10000 |
|---|---|---|---|
| Linear coefficient of thermal expansion | -30℃-30℃ | ASTM D-696 | 80 µm/mK |
| vicat | 10N | ISO 306/A | 145 °C |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75/B | 110 °C |
| Linear coefficient of thermal expansion | 23℃-80℃ | ASTM D-696 | 110 µm/mK |