Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
AES SK50 UMG JAPAN
DIALAC®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UMG JAPAN/SK50 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 100 |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/SK50 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 65.0 Mpa |
| tensile strength | 23℃ | ISO 527-2 | 42.0 Mpa |
| Flexural modulus | 23℃ | ISO 178 | 2200 Mpa |
| Charpy Notched Impact Strength | -30℃ | ISO 179 | 8.0 kJ/m² |
| Flexural modulus | 23°C | ISO 178 | 2200 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2050 Mpa |
| Rockwell hardness | 23℃ | ISO 2039-2 | 100 R 计秤 |
| Tensile modulus | 23℃ | ISO 527-2 | 2050 Mpa |
| bending strength | 23℃ | ISO 178 | 65.0 Mpa |
| tensile strength | 23°C | ISO 527-2 | 42.0 Mpa |
| flammability | Test Condition | Test Method | UMG JAPAN/SK50 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | UMG JAPAN/SK50 |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.70-0.90 % |
| MD，23℃ | ISO 294-4 | 0.70 - 0.90 % | |
| Melt volume flow rate | 220℃/2.16 kg | ISO 1133 | 17.0 cm3/10min |
| 220°C/10.0kg | ISO 1133 | 17.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/SK50 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 0.000090 cm/cm/℃ |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 78.0 °C |
| 1.80MPa，未退火，HDT | ISO 75-2/Af | 78.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-05 cm/cm/°C |
| UL flame retardant rating | 1.50mm | UL 94 | HB |