Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP V400P CELANESE USA
VECTRA®
film
Chemical resistance、transparent、Halogen-free、Barrier resin、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | CELANESE USA/V400P |
|---|---|---|---|
| OTr | 23°C2 | DIN 53380-3 | 1.4 cc-25µm/m²-day-atm |
| 23°C3 | DIN 53380-3 | 1.3 cc-25µm/m²-day-atm | |
| Water Vapor Transmission Rate | 38°C | DIN 53122 | 0.400 g-25µm/(m² day-atm) |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/V400P |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 14400 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 151 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.6 % |
| physical property | Test Condition | Test Method | CELANESE USA/V400P |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.040 % |
| melt mass-flow rate | 230°C/2.16 kg | 内部方法 | 14 g/10 min |
| Thermal performance | Test Condition | Test Method | CELANESE USA/V400P |
|---|---|---|---|
| Glass Transition Temperature | ISO 3146 | 110 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 111 °C |
| injection | Test Condition | Test Method | CELANESE USA/V400P |
|---|---|---|---|
| drying time | 8.0 to 24 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Temperature in the middle of the barrel | 205 to 215 °C | ||
| Temperature at the rear of the barrel | 185 to 195 °C | ||
| Processing (melt) temperature | 225 to 235 °C | ||
| drying temperature | 90 °C | ||
| Temperature at the front of the material cylinder | 205 to 215 °C | ||
| Spray nozzle temperature | 200 to 210 °C |