Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT S600F20 BK851 DUPONT USA
Cristin®
Electronic and electrical components,Automotive Applications,Industrial applications,Automotive Applications
Medium viscosity,Good dimensional stabilit,Good resistance to chemic
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-1 | 22 % |
| Impact resistance | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.5 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Odor | VDA270 | 3.00 | |
| Thermal Desorption Analysis of Organic Emissions | VDA278 | 1.00 µg/g |
| thermal performance | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| UL flame retardant rating | 3.00 mm | UL94 | HB |
| Heat Deflection Temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 115 °C |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| MD：55to160°C | ISO 11359-2 | 1.9E-04 cm/cm/°C | |
| 平行流动方向，23 to 55°C (73 to 130°F) | ISO 11359-1 | 0.00013 cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | 55.0 °C | |
| melting temperature | ISO 11357-3 | 225 °C | |
| Heat Deflection Temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 60.0 °C |
| UL flame retardant rating | 1.50 mm | UL94 | HB |
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 50.0 °C |
| 1.8 Mpa，未退火，HDT | ISO 75B-1 | 60 ℃ | |
| melting temperature | ISO 3146 | 225 ℃ | |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| PeakCrystallizationTemperature | ISO 11357-3 | 192 °C | |
| Heat Deflection Temperature | 0.45 Mpa，未退火，HDT | ISO 75B-1 | 180 ℃ |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| vicat | ISO 306/B50 | 175 °C | |
| Linear coefficient of thermal expansion | TD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| TD：55to160°C | ISO 11359-2 | 2E-04 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 180 °C |
| Linear coefficient of thermal expansion | 垂直流动方向，23 to 55°C (73 to 130°F) | ISO 11359-1 | 0.00013 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Tensile stress | 23 ℃, 50 mm/min，屈服 | ISO 527-1 | 58 MPa |
| bending strength | ISO 178 | 85 MPa | |
| Nominal tensile fracture strain | ISO 527-2 | 40 % | |
| tensile strength | 屈服 | ISO 527-2 | 58.0 Mpa |
| bending strength | ISO 178 | 85.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.0 % |
| elongation | 23 ℃, 50 mm/min，屈服 | ISO 527-1 | 7.6 % |
| Tensile creep modulus | 1000h | ISO 899-1 | 1800 MPa |
| Tensile modulus | 23 ℃, 1.0 mm/min | ISO 527-1 | 2600 MPa |
| Impact strength of simply supported beam without notch | -30 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Charpy Notched Impact Strength | -30 ℃, Type 1, Edgewise, Notch A | ISO 179 | 4 KJ/m |
| Impact strength of cantilever beam gap | 23 ℃, Type 1, Notch A | ISO 180 | 4 KJ/m |
| Charpy Notched Impact Strength | 23 ℃, Type 1, Edgewise, Notch A | ISO 179 | 4.5 KJ/m |
| Tensile creep modulus | 1hr | ISO 899-1 | 2600 Mpa |
| Tensile modulus | ISO 527-2 | 2500 Mpa | |
| Nominal fracture strain | 23 ℃, 50 mm/min | ISO 527-1 | 40 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1800 Mpa |
| flexural modulus | ISO 178 | 2200 Mpa | |
| Impact strength of simply supported beam without notch | 23 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Electrical performance | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| dielectric strength | IEC 60243-1 | 26 KV/mm | |
| Dissipation Factor | 100Hz | IEC 60250 | 7.9E-04 |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Surface Resistivity | IEC 60093 | 1E+12 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| Physical properties | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.20 % |
| ThermalConductivityofMelt | 0.21 W/m/K | ||
| Water absorption rate | Sat/23C | ISO 62 | 0.40 % |
| density | ISO 1183 | 1.31 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 1.6 % |
| Flow | ISO 294-4 | 1.7 % | |
| MediumDensity | 1.11 g/cm³ | ||
| Water absorption rate | 23C/59RH | ISO 62 | 0.2 % |
| shrinkage rate | MD | ISO 294-4 | 1.7 % |
| viscosity number | ISO 307 | 130 cm³/g | |
| SpecificHeatCapacity of Melt | 2110 J/kg/°C | ||
| shrinkage rate | Across Flow | ISO 294-4 | 1.6 % |
| density | ISO 1183 | 1.31 g/cm | |
| Ejection Temperature | 170 °C | ||
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.40 % |
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 19 g/10min |
| flammability | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| Fogging-G-value | condensate | ISO 6452 | 0.0 g |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | SE | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 22 % |