PES JF1004 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic field、mechanical、Bearing retainer
High temperature creep re、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/JF1004 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 73 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 4.49 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.1 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 15.8 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/JF1004 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 7590 Mpa | |
| ASTM D638 | 7360 Mpa | ||
| elongation | 断裂 | ASTM D638 | 2.8 % |
| bending strength | ISO 178 | 183 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.9 % |
| Flexural modulus | ISO 178 | 6420 Mpa | |
| bending strength | ASTM D790 | 186 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 114 Mpa |
| 断裂 | ISO 527-2 | 109 Mpa | |
| Flexural modulus | ASTM D790 | 6690 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/JF1004 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.50-0.70 % |
| MD：24小时 | ASTM D955 | 0.50-0.70 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.40 % |
| 平衡,23°C,50%RH | ISO 62 | 0.74 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.60-0.80 % |
| TD:24小时 | ISO 294-4 | 0.60-0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/JF1004 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 205 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 206 °C |