PC/ABS Loyblend® TA-1004 Colour Image Plastic Compound Sdn. Bhd. (CIPC)
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Colour Image Plastic Compound Sdn. Bhd. (CIPC)/Loyblend® TA-1004 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 830 J/m |
| hardness | Test Condition | Test Method | Colour Image Plastic Compound Sdn. Bhd. (CIPC)/Loyblend® TA-1004 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | Colour Image Plastic Compound Sdn. Bhd. (CIPC)/Loyblend® TA-1004 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | >50 % |
| tensile strength | ASTM D638 | 57.0 MPa | |
| Flexural modulus | ASTM D790 | 2380 MPa | |
| Tensile modulus | ASTM D638 | 2850 MPa | |
| bending strength | ASTM D790 | 92.0 MPa |
| flammability | Test Condition | Test Method | Colour Image Plastic Compound Sdn. Bhd. (CIPC)/Loyblend® TA-1004 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Colour Image Plastic Compound Sdn. Bhd. (CIPC)/Loyblend® TA-1004 |
|---|---|---|---|
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 9.0 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.40to0.60 % |
| Water absorption rate | 24hr | ASTM D570 | 0.10 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 16 g/10min |
| density | ASTM D792 | 1.15 g/cm³ |
| Thermal performance | Test Condition | Test Method | Colour Image Plastic Compound Sdn. Bhd. (CIPC)/Loyblend® TA-1004 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,4.00mm，HDT | ASTM D648 | 127 °C |
| 1.8MPa,未退火,4.00mm，HDT | ASTM D648 | 110 °C |