PC EXL9134 BK1A068 SABIC INNOVATIVE NANSHA
LEXAN™ 
Lighting applications、Electronic and Electrical、Aerospace Applications、Plastic bag
High mobility、High ductility at low tem、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL9134 BK1A068
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA35 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376367.0 J
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL9134 BK1A068
Tensile modulus--2ASTM D6382100 Mpa
tensile strength 屈服3ASTM D63858.0 Mpa
elongation断裂3ASTM D638120 %
断裂ISO 527-2/50110 %
Flexural modulus--5ISO 1782100 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D79092.0 Mpa
--5,6ISO 17887.0 Mpa
Flexural modulus50.0 mm 跨距4ASTM D7902400 Mpa
tensile strength 断裂ISO 527-2/5057.0 Mpa
屈服ISO 527-2/5056.0 Mpa
elongation屈服ISO 527-2/506.0 %
屈服3ASTM D6386.0 %
tensile strength 断裂3ASTM D63859.0 Mpa
Tensile modulus--ISO 527-2/12000 Mpa
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL9134 BK1A068
Hot filament ignition temperature1.5 mmIEC 60695-2-13825 °C
UL flame retardant rating3.0 mmUL 945VA
Hot filament ignition temperature3.0 mmIEC 60695-2-13825 °C
UL flame retardant rating1.5 mmUL 94V-0
Burning wire flammability index1.5 mmIEC 60695-2-12960 °C
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL9134 BK1A068
Water absorption rate平衡, 23°C, 50% RHISO 620.15 %
Melt volume flow rate300°C/1.2 kgISO 113315.0 cm3/10min
Outdoor applicabilityUL 746Cf1
melt mass-flow rate300°C/1.2 kgASTM D123816 g/10 min
Water absorption rate饱和, 23°CISO 620.40 %
Shrinkage rate3.20 mm，Flow内部方法0.40 - 0.80 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL9134 BK1A068
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8316.1E-5 cm/cm/°C
vicat--ISO 306/B120141 °C
--ASTM D152510140 °C
Linear coefficient of thermal expansion横向 : -40°CISO 11359-26.2E-5 cm/cm/°C
vicat--ISO 306/B50139 °C
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDTISO 75-2/Af118 °C
RTI ImpUL 746115 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8316.2E-5 cm/cm/°C
RTIUL 746120 °C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D648123 °C
RTI ElecUL 746125 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/EXL9134 BK1A068
screw speed40 to 70 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature295 to 315 °C
drying temperature120 °C
Suggested injection volume40 to 60 %
drying time3.0 to 4.0 hr
Temperature in the middle of the barrel280 to 305 °C
Temperature at the rear of the barrel270 to 295 °C
Exhaust hole depth0.025 to 0.076 mm
Temperature at the front of the material cylinder295 to 315 °C
Back pressure0.300 to 0.700 Mpa
Temperature70 to 95 °C
Spray nozzle temperature290 to 310 °C