PA66 RN001S SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical applications、Home appliance components
Thermal stability、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/RN001S |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 231 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 223 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 76.7 °C | |
| 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 301 °C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/RN001S |
|---|---|---|---|
| Tensile Strain | 屈服 | ISO527-2 | 2.1 % |
| Tensile Elongation | 断裂 | ASTMD638 | 3.8 % |
| Flexural Modulus | ASTMD790 | 3450 Mpa | |
| Tensile Stress | 屈服 | ISO527-2 | 69.0 Mpa |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.75 |
| Tensile Modulus | ISO527-2/1 | 3910 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 84.1 Mpa |
| Flexural Modulus | ISO178 | 3400 Mpa | |
| Coefficient of Friction | Static | ASTMD3702Modified | 0.55 |
| Tensile Elongation | 屈服 | ASTMD638 | 2.9 % |
| Specific Wear Rate | ASTMD3702Modified | 103 10^-10in^5-min/ft-lb-hr | |
| Tensile Strain | 断裂 | ISO527-2 | 42 % |
| Tensile Stress | 69.0 Mpa | ||
| Flexural Stress | ISO178 | 107 Mpa | |
| Tensile Modulus | ASTMD638 | 4140 Mpa | |
| Tensile Strength | 断裂 | 84.1 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/RN001S |
|---|---|---|---|
| Modeling Shrinkage | TD:24小时 | ISO294-4 | 1.0 % |
| MD:24小时 | 1.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/RN001S |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 2.30 J |
| 23°C | ISO180/1U | 54 kJ/m² | |
| Notched Izod Impact Strength | ISO180/1A | 2.8 kJ/m² |