Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPEE P-150B TOYOBO JAPAN
PELPRENE™
currency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodTOYOBO JAPAN/P-150B
Shore hardness邵氏DASTM D224057
Electrical performanceTest ConditionTest MethodTOYOBO JAPAN/P-150B
Volume resistivityASTM D2572E+14 ohms·cm
dielectric strengthASTM D14930 KV/mm
Mechanical propertiesTest ConditionTest MethodTOYOBO JAPAN/P-150B
Taber abraser1000CyclesASTM D104410.0 mg
elongation断裂ASTM D638500 %
Compression ModulusASTM D69519.1 Mpa
tensile strength 屈服ASTM D63838.0 Mpa
Flexural modulusASTM D790289 Mpa
flammabilityTest ConditionTest MethodTOYOBO JAPAN/P-150B
UL flame retardant ratingUL 94HB
elastomerTest ConditionTest MethodTOYOBO JAPAN/P-150B
compression setASTM D39560 %
tear strengthASTM D624177 kN/m
tensile strength 50%应变ASTM D41219.6 Mpa
physical property Test ConditionTest MethodTOYOBO JAPAN/P-150B
melt mass-flow rate230°C/2.16kgASTM D123820 g/10min
Shrinkage rateMD:2.00mmASTM D9551.3 %
Water absorption rate平衡,23°C,65%RHASTM D5700.36 %
Thermal performanceTest ConditionTest MethodTOYOBO JAPAN/P-150B
Heat distortion temperature1.8MPa,未退火,HDTASTM D648117 °C
vicatASTM D1525190 °C
brittle temperatureASTM D746-65.0 °C
Linear coefficient of thermal expansionMDASTM D6961.4E-04 cm/cm/°C
melting temperatureDSC212 °C