LLDPE XLF175 Ixom Operations Pty Ltd
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | Ixom Operations Pty Ltd/ XLF175 |
|---|---|---|---|
| tensile strength | MD:屈服,30µm | ASTM D882 | 11.0 MPa |
| MD:断裂,30µm | ASTM D882 | 23.0 MPa | |
| TD:断裂,30µm | ASTM D882 | 16.0 MPa | |
| elongation | TD:断裂,30µm | ASTM D882 | 790 % |
| film thickness | 30 µm | ||
| Secant modulus | 2%正割,MD:30µm | ASTM D882 | 270 MPa |
| Dart impact | 30µm,吹塑薄膜 | ASTM D1709 | 55 g |
| Secant modulus | 2%正割,TD:30µm | ASTM D882 | 340 MPa |
| tensile strength | TD:屈服,30µm | ASTM D882 | 14.0 MPa |
| Elmendorf tear strength | MD:30µm | ASTM D1922 | 340 g |
| elongation | MD:断裂,30µm | ASTM D882 | 280 % |
| Elmendorf tear strength | TD:30µm | ASTM D1922 | 150 g |
| Mechanical properties | Test Condition | Test Method | Ixom Operations Pty Ltd/ XLF175 |
|---|---|---|---|
| coefficient of friction | 吹塑薄膜 | ASTM D1894 | 0.40 |
| optical performance | Test Condition | Test Method | Ixom Operations Pty Ltd/ XLF175 |
|---|---|---|---|
| Haze ratio | 30.0µm,吹塑薄膜 | ASTM D1003 | 8.0 % |
| gloss | 30.0µm,吹塑薄膜 | ASTM D2457 | 60 |
| physical property | Test Condition | Test Method | Ixom Operations Pty Ltd/ XLF175 |
|---|---|---|---|
| density | ASTM D1505 | 0.928 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 4.0 g/10min |