PBT 420SEO-1001 SABIC INNOVATIVE THAILAND
VALOX™
Lawn equipment、Garden equipment、Industrial applications、Automotive External Parts、Electrical field、Electronic field、Architectural application、Outdoor applications、Electrical appliances、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Automotive interior parts、Casters、Household goods、Petroleum Applications、Natural gas supplies、sporting goods、Textile application、Lighting applications
Glass fiber reinforced、dimensional stability 、High rigidity、high strength、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SEO-1001 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C8 | ISO 180/1U | 45 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C8 | ISO 180/1U | 45 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 6.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 620 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 5.00 J |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 50 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SEO-1001 |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 119 |
| ball-indentation hardness | H 358/30 | ISO 2039-1 | 118 Mpa |
| Rockwell hardness | R 级 | ASTM D785 | 119 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SEO-1001 |
|---|---|---|---|
| tensile strength | 屈服4 | ASTM D638 | 120 Mpa |
| 断裂 | ISO 527-2/5 | 120 Mpa | |
| elongation | 断裂4 | ASTM D638 | 2.0 % |
| Tensile modulus | --3 | ASTM D638 | 12000 Mpa |
| Flexural modulus | 50.0 mm 跨距5 | ASTM D790 | 9800 Mpa |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 22.0 mg |
| Flexural modulus | --6 | ISO 178 | 9500 Mpa |
| bending strength | -- | ISO 178 | 180 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 1.9 % |
| tensile strength | 屈服 | ISO 527-2/5 | 120 Mpa |
| elongation | 屈服4 | ASTM D638 | 2.0 % |
| tensile strength | 断裂4 | ASTM D638 | 120 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 10000 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 1.9 % |
| bending strength | 断裂, 50.0 mm 跨距5 | ASTM D790 | 186 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SEO-1001 |
|---|---|---|---|
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 24 KV/mm |
| Volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| dielectric constant | 100 Hz | ASTM D150 | 3.80 |
| dielectric strength | 0.800 mm, 在油中 | IEC 60243-1 | 23 KV/mm |
| dielectric constant | 50 Hz | IEC 60250 | 3.30 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 B | IEC 60112 | PLC 4 |
| dielectric constant | 1 MHz | ASTM D150 | 3.70 |
| Dissipation Factor | 50 Hz | IEC 60250 | 1.0E-3 |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| Compared to the Leakage Tracking Index (CTI) | -- | IEC 60112 | PLC 3 |
| dielectric strength | 1.60 mm, 在油中 | IEC 60243-1 | 22 KV/mm |
| dielectric constant | 60 Hz | IEC 60250 | 3.30 |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.010 |
| 100 Hz | ASTM D150 | 2.0E-3 | |
| 60 Hz | IEC 60250 | 1.0E-3 | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 19 KV/mm |
| arc resistance | ASTM D495 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 16 KV/mm |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.020 |
| dielectric constant | 1 MHz | IEC 60250 | 3.30 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SEO-1001 |
|---|---|---|---|
| UL flame retardant rating | 0.71 mm | UL 94 | V-0 |
| 0.40 mm | UL 94 | V-2 | |
| 2.0 mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ISO 4589-2 | 32 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SEO-1001 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.070 % |
| Shrinkage rate | 流动 2 | 内部方法 | 0.10 - 0.50 % |
| 横向流动 2 | 内部方法 | 0.40 - 0.80 % | |
| 横向流动 : 3.20 mm | 内部方法 | 0.50 - 1.0 % | |
| Outdoor applicability | UL 746C | f2 | |
| melt mass-flow rate | 250°C/5.0 kg | ASTM D1238 | 42 g/10 min |
| Melt volume flow rate | 250°C/5.0 kg | ISO 1133 | 29.0 cm3/10min |
| Specific volume | ASTM D792 | 0.610 cm³/g | |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.090 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SEO-1001 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 2.5E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距9，HDT | ISO 75-2/Ae | 195 °C |
| Linear coefficient of thermal expansion | 横向 : 23 到 80°C | ISO 11359-2 | 1.2E-4 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 2.5E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 8.9E-5 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 212 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDT | ISO 75-2/Af | 200 °C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI | UL 746 | 140 °C | |
| thermal conductivity | ISO 8302 | 0.25 W/m/K | |
| vicat | -- | ASTM D152510 | 200 °C |
| -- | ISO 306/A50 | 220 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距9，HDT | ISO 75-2/Be | 220 °C |
| RTI Imp | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 8.9E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 200 °C |
| RTI Elec | UL 746 | 130 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SEO-1001 |
|---|---|---|---|
| screw speed | 50 to 80 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 255 to 275 °C | ||
| drying temperature | 120 °C | ||
| Suggested injection volume | 40 to 80 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 250 to 270 °C | ||
| Temperature at the rear of the barrel | 245 to 265 °C | ||
| Exhaust hole depth | 0.025 to 0.038 mm | ||
| Temperature at the front of the material cylinder | 255 to 275 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 65 to 90 °C | ||
| Spray nozzle temperature | 250 to 270 °C |