PA66 LUBEMID A26 TF10 NATURAL LUBEN PLAST srl
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LUBEN PLAST srl/LUBEMID A26 TF10 NATURAL |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C4 | ASTM D256 | 3.0to4.5 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 2.5to3.5 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 45to55 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40to50 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256A | 30to45 J/m |
| 23°C | ISO 180/A | 3.0to3.5 kJ/m² | |
| 23°C3 | ASTM D256 | 45to55 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LUBEN PLAST srl/LUBEMID A26 TF10 NATURAL |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 2400to2800 MPa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 60.0to70.0 MPa |
| 屈服 | ISO 527-2/1A/5 | 60.0to70.0 MPa | |
| Tensile strain | 屈服 | ISO 527-2/1A/5 | 5.0to7.0 % |
| 断裂 | ISO 527-2/1A/5 | 5.0to7.0 % | |
| Flexural modulus | ISO 178 | 2300to2700 MPa | |
| bending strength | ISO 178 | 70.0to80.0 MPa |
| physical property | Test Condition | Test Method | LUBEN PLAST srl/LUBEMID A26 TF10 NATURAL |
|---|---|---|---|
| density | ISO 1183/A | 1.20to1.21 g/cm³ |
| Thermal performance | Test Condition | Test Method | LUBEN PLAST srl/LUBEMID A26 TF10 NATURAL |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 225to235 °C |
| melting temperature | 内部方法 | 250to265 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220to230 °C |
| vicat | -- | ISO 306/A120 | 245to255 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 220to230 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 70.0to80.0 °C |