PC/ABS C7210A-701 SABIC INNOVATIVE US
CYCOLAC™
Electronic field、Electrical field、Thin walled components
High mobility、Flame retardant、Filler: Talc filler
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A-701 |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 47.5 J |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 1900 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A-701 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3520 Mpa | |
| elongation | 断裂 | ASTM D638 | 80 % |
| 屈服 | ASTM D638 | 3.6 % | |
| tensile strength | 断裂 | ASTM D638 | 49.0 Mpa |
| 屈服 | ASTM D638 | 63.4 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 3140 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 106 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A-701 |
|---|---|---|---|
| UL flame retardant rating | 1.98mm | UL 94 | 5VB |
| 1.19mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A-701 |
|---|---|---|---|
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 16 g/10min |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.30-0.50 % |
| TD:3.20mm | 内部方法 | 0.40-0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/C7210A-701 |
|---|---|---|---|
| vicat | ASTM D15256 | 102 °C | |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 92.2 °C |
| RTI Imp | UL 746 | 85.0 °C | |
| RTI | UL 746 | 90.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 82.2 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 5.9E-05 cm/cm/°C |
| RTI Elec | UL 746 | 90.0 °C |