ASA+PC SCANBLEND FS8 UV4 POLYKEMI SWEDEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | POLYKEMI SWEDEN/SCANBLEND FS8 UV4 | |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Flexural modulus | 23°C | ISO 178 | 2500 MPa |
| Shrinkage rate | MD | ISO 294-4 | 0.50to0.70 % |
| Tensile strain | 屈服 | ISO 527-2 | 7.0 % |
| density | ISO 1183 | 1.17 g/cm³ | |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 50 kJ/m² |
| Shrinkage rate | TD | ISO 294-4 | 0.50to0.70 % |
| bending strength | ISO 178 | 85.0 MPa | |
| vicat | ISO 306/B50 | 134 °C | |
| tensile strength | ISO 527-2 | 50.0 MPa | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 132 °C |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 20 g/10min |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 122 °C |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 650 °C |