PPS OL-4030 SABIC INNOVATIVE US
LNP™ LUBRICOMP™ 
Automotive Applications
Carbon fiber reinforced、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/OL-4030
Suspended wall beam without notch impact strength23°CISO 180/1U4.8 kJ/m²
Dart impact23°C,TotalEnergyASTM D37631.00 J
Multi axis Instrumented Impact EnergyISO 6603-20.400 J
Impact strength of cantilever beam gap23°CISO 180/1A2.2 kJ/m²
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/OL-4030
Tensile modulusISO 527-2/13370 Mpa
ASTM D6383590 Mpa
tensile strength 断裂ISO 527-2/520.0 Mpa
elongation断裂ASTM D6380.60 %
bending strengthISO 17856.0 Mpa
Flexural modulusISO 1783320 Mpa
Tensile strain断裂ISO 527-2/50.60 %
tensile strength 断裂ASTM D63821.0 Mpa
Flexural modulus50.0mm跨距ASTM D7903870 Mpa
bending strength断裂,50.0mm跨距ASTM D79065.0 Mpa
physical property Test ConditionTest MethodSABIC INNOVATIVE US/OL-4030
Shrinkage rateMD：24小时ASTM D9550.90-2.0 %
Water absorption rate24hr,50%RHASTM D5700.020 %
平衡,23°C,50%RHISO 620.040 %
Shrinkage rateTD：24hrASTM D9551.0-3.0 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/OL-4030
Heat distortion temperature0.45MPa,Unannealed,64.0mmSpan，HDTISO 75-2/Bf178 °C
Linear coefficient of thermal expansionMD：-30到30°CASTM D6966E-05 cm/cm/°C
TD：-30to30°CASTM D6966.6E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,3.20mm，HDTASTM D648175 °C
1.8MPa,未退火,64.0mm跨距，HDTISO 75-2/Af109 °C
1.8MPa,未退火,3.20mm，HDTASTM D648108 °C