TPV 3150N DSM HOLAND
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | DSM HOLAND/3150N |
|---|---|---|---|
| Shore hardness | 邵氏A,5秒,注塑 | ISO 868 | 56 |
| 邵氏A,5秒,挤塑 | ASTM D2240 | 54 | |
| 邵氏A,5秒,挤塑 | ISO 868 | 54 | |
| 邵氏A,5秒,注塑 | ASTM D2240 | 56 |
| Supplementary Information | Test Condition | Test Method | DSM HOLAND/3150N |
|---|---|---|---|
| ApparentShearViscosity-Capillary,@206/s | 200°C | ISO 11443 | 270 Pa·s |
| 200°C | ASTM D3835 | 270 Pa·s |
| flammability | Test Condition | Test Method | DSM HOLAND/3150N |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| elastomer | Test Condition | Test Method | DSM HOLAND/3150N |
|---|---|---|---|
| elongation | 断裂 | ASTM D412 | 600 % |
| compression set | 23°C,22hr | ISO 815 | 20 % |
| 70°C,22hr | ASTM D395 | 32 % | |
| 125°C,70hr | ASTM D395 | 52 % | |
| elongation | 断裂 | ISO 37 | 600 % |
| tensile strength | 流量:断裂 | ASTM D412 | 4.10 Mpa |
| 断裂 | ISO 37 | 5.10 Mpa | |
| compression set | 125°C,70hr | ISO 815 | 52 % |
| tensile strength | 横向流量:100%应变 | ASTM D412 | 1.90 Mpa |
| compression set | 23°C,22hr | ASTM D395 | 20 % |
| elongation | 流量:断裂 | ISO 37 | 240 % |
| tensile strength | 流量:100%应变 | ISO 37 | 3.00 Mpa |
| 流量:断裂 | ISO 37 | 4.10 Mpa | |
| compression set | 70°C,22hr | ISO 815 | 32 % |
| elongation | 流量:断裂 | ASTM D412 | 240 % |
| tear strength | 横向流量 | ASTM D624 | 24.5 kN/m |
| 横向流量 | ISO 34-1 | 24 kN/m | |
| tensile strength | 断裂 | ASTM D412 | 5.10 Mpa |
| 横向流量:100%应变 | ISO 37 | 1.90 Mpa | |
| 流量:100%应变 | ASTM D412 | 3.00 Mpa |
| aging | Test Condition | Test Method | DSM HOLAND/3150N |
|---|---|---|---|
| Change rate of tensile strength in air | 100%应变,150°C,168hr，横向 | ASTM D573 | 5.0 % |
| Change rate of ultimate elongation in air | 135°C,1000hr，横向 | ASTM D573 | -7.0 % |
| Change rate of hardness (Shore) in the air | 邵氏A,150°C,168hr | ASTM D573 | 2.0 |
| Change rate of tensile strength in air | 100%应变150°C,168hr，横向 | ISO 188 | 5.0 % |
| Tensile stress change rate | 135°C,1000hr，断裂 | ISO 188 | -7.0 % |
| volume change | 125°C,70hr,在IRM903油中 | ASTM D471 | 130 % |
| Change rate of tensile strength in air | 100%应变135°C,1000hr，横向 | ISO 188 | 7.0 % |
| 135°C,1000hr，横向 | ISO 188 | -6.0 % | |
| volume change | 125°C,70hr,在IRM903油中 | ISO 1817 | 130 % |
| Tensile stress change rate | 150°C,168hr，断裂 | ISO 188 | 8.0 % |
| Change rate of tensile strength in air | 100%应变,135°C,1000hr，横向 | ASTM D573 | 7.0 % |
| Change rate of ultimate elongation in air | 150°C,168hr，横向 | ASTM D573 | 8.0 % |
| Change rate of hardness (Shore) in the air | 邵氏A,135°C,1000hr | ISO 188 | 1.0 |
| 邵氏A,150°C,168hr | ISO 188 | 2.0 | |
| Change rate of tensile strength in air | 135°C,1000hr，横向 | ASTM D573 | -6.0 % |
| 150°C,168hr，横向 | ASTM D573 | 7.0 % | |
| Change rate of hardness (Shore) in the air | 邵氏A,135°C,1000hr | ASTM D573 | 1.0 |
| Change rate of tensile strength in air | 150°C,168hr，横向 | ISO 188 | 7.0 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/3150N |
|---|---|---|---|
| RTI Imp | UL 746 | 50.0 °C | |
| RTI Str | UL 746 | 50.0 °C | |
| RTI Elec | UL 746 | 50.0 °C |