PLA+PMMA Plexiglas® Rnew® B514 Altuglas International of Arkema Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Altuglas International of Arkema Inc./Plexiglas® Rnew® B514 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 110 J/m |
| Supplementary Information | Test Condition | Test Method | Altuglas International of Arkema Inc./Plexiglas® Rnew® B514 |
|---|---|---|---|
| RenewableCarbonConent | 28 % | ||
| ASTMClassification | ASTM D788 | PMMA0231V-1 |
| hardness | Test Condition | Test Method | Altuglas International of Arkema Inc./Plexiglas® Rnew® B514 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 49 |
| Mechanical properties | Test Condition | Test Method | Altuglas International of Arkema Inc./Plexiglas® Rnew® B514 |
|---|---|---|---|
| bending strength | 屈服 | ASTM D790 | 50.3 MPa |
| Flexural modulus | ASTM D790 | 1590 MPa | |
| Tensile modulus | ASTM D638 | 1590 MPa | |
| tensile strength | 屈服 | ASTM D638 | 35.9 MPa |
| optical performance | Test Condition | Test Method | Altuglas International of Arkema Inc./Plexiglas® Rnew® B514 |
|---|---|---|---|
| Haze ratio | 3180µm | ASTM D1003 | <5.0 % |
| refractive index | ASTM D542 | 1.490 | |
| transmissivity | 3180µm | ASTM D1003 | 86.0 % |
| physical property | Test Condition | Test Method | Altuglas International of Arkema Inc./Plexiglas® Rnew® B514 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.20to0.60 % |
| Water absorption rate | 24hr | ASTM D570 | 0.30 % |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 3.9 g/10min |
| density | ASTM D792 | 1.16 g/cm³ |
| Thermal performance | Test Condition | Test Method | Altuglas International of Arkema Inc./Plexiglas® Rnew® B514 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Annealed，HDT | ASTM D648 | 67.8 °C |
| vicat | ASTM D15253 | 77.8 °C |