PP TRC 152N LYONDELLBASELL HOLAND
HOSTACOM
Automotive sector、Automotive interior parts
Low gloss、enhance、Mineral reinforcement、Mineral filler、20% filler by weight、Impact modification、Low glossiness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL HOLAND/TRC 152N |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eU | 无断裂 |
| Tensile strain | 屈服, 23℃ | ISO 527-2/50 | 4.0 % |
| Flexural modulus | 23℃ | ISO 178 | 1700 Mpa |
| Charpy Notched Impact Strength | -30℃ | ISO 179/1eA | 5.0 kJ/m² |
| tensile strength | 屈服, 23℃ | ISO 527-2/50 | 18.0 Mpa |
| physical property | Test Condition | Test Method | LYONDELLBASELL HOLAND/TRC 152N |
|---|---|---|---|
| melt mass-flow rate | 230℃/2.16 kg | ISO 1133 | 16 g/10 min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/TRC 152N |
|---|---|---|---|
| vicat | ISO 306/A50 | 125 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 95.0 °C |
| vicat | ISO 306/B50 | 48.0 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | DIN 53461 | 51.0 °C |