Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 408L DUPONT USA
Zytel®
Industrial machinery、Industrial applications、Non specific food applica
High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/408L |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 15 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/408L |
|---|---|---|---|
| Odor | VDA270 | 4.00 | |
| Emissions of Organic Compounds | VDA277 | 35.0 µgC/g |
| film | Test Condition | Test Method | DUPONT USA/408L |
|---|---|---|---|
| Tensile strain | Yield，MD | ISO 527-3 | 6.0 % |
| Electrical performance | Test Condition | Test Method | DUPONT USA/408L |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.20 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.020 |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/408L |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2200 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| Nominal tensile fracture strain | ISO 527-2 | 35 % | |
| Tensile strain | 屈服 | ISO 527-2 | 6.0 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| tensile strength | 屈服 | ISO 527-2 | 61.0 Mpa |
| flammability | Test Condition | Test Method | DUPONT USA/408L |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 19 % | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/408L |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.5 % |
| MD | ISO 294-4 | 1.5 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 7.0 % |
| MediumDensity | 0.950 g/cm³ | ||
| Ejection Temperature | 190 °C | ||
| density | ISO 1183 | 1.09 g/cm³ | |
| SpecificHeatCapacity of Melt | 2600 J/kg/°C | ||
| ThermalConductivityofMelt | 0.16 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 2.2 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/408L |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 263 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 155 °C |
| vicat | ISO 306/B50 | 210 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 66.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.3E-04 cm/cm/°C |