PPS OCL-4532 LEX SABIC INNOVATIVE US
LNP™ STAT-KON™
Electronic and electrical components
Flame retardant,Filler: Carbon fiber rein
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/OCL-4532 LEX |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 430 J/m |
| 23°C3 | ISO 180/1U | 24 kJ/m² | |
| Dart impact | -- | ISO 6603-2 | 2.53 J |
| 23°C,EnergyatPeakLoad | ASTM D3763 | 8.40 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/OCL-4532 LEX |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 11200 Mpa |
| tensile strength | 断裂 | ASTM D638 | 127 Mpa |
| 断裂 | ISO 527-2 | 125 Mpa | |
| Flexural modulus | -- | ISO 178 | 9740 Mpa |
| Wear factor | Washer | ASTM D3702Modified | 39.0 10^-10in^5-min/ft-lb-hr |
| bending strength | -- | ISO 178 | 172 Mpa |
| elongation | 断裂 | ASTM D638 | 1.6 % |
| bending strength | -- | ASTM D790 | 168 Mpa |
| coefficient of friction | Static | ASTM D3702Modified | 0.33 |
| Tensile modulus | -- | ISO 527-2/1 | 11200 Mpa |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.32 |
| Flexural modulus | -- | ASTM D790 | 9720 Mpa |
| elongation | 断裂 | ISO 527-2 | 1.4 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/OCL-4532 LEX |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+2-1.0E+4 ohms |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/OCL-4532 LEX |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.50-0.70 % |
| TD:24小时 | ASTM D955 | 0.60-0.80 % | |
| MD:24小时 | ASTM D955 | 0.50-0.70 % | |
| TD:24小时 | ISO 294-4 | 0.60-0.80 % |