Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RF-1004FR BK SABIC INNOVATIVE US
LNP™ THERMOCOMP™ 
Automotive components,Electronic and electrical components
Thermal stability,High temperature resistan,high strength,Filler: Glass fiber reinf,20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/RF-1004FR BK
Dart impact23°C,EnergyatPeakLoadASTM D376311.4 J
Impact strength of cantilever beam gap23°CISO 180/1A8.6 kJ/m²
Multi axis Instrumented Impact EnergyISO 6603-22.49 J
Suspended wall beam without notch impact strength23°CISO 180/1U56 kJ/m²
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/RF-1004FR BK
Heat Deflection Temperature0.45MPa,未退火,3.20mmASTM D648260 °C
1.8MPa,未退火,3.20mmASTM D648247 °C
1.8MPa,未退火,64.0mm跨距ISO 75-2/Af221 °C
Linear coefficient of thermal expansionTD：-40到40°CASTME8317.9E-05 cm/cm/°C
TD：-40到40°CISO 11359-27.9E-05 cm/cm/°C
MD：-40到40°CISO 11359-23.9E-05 cm/cm/°C
MD：-40到40°CASTME8313.8E-05 cm/cm/°C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/RF-1004FR BK
bending strengthISO 178242 Mpa
ASTM D790231 Mpa
coefficient of frictionStaticASTM D3702Modified0.52
DynamicASTM D3702Modified0.68
elongation断裂ASTM D6383.6 %
flexural modulusASTM D7905860 Mpa
ISO 1787000 Mpa
Tensile modulusASTM D6387170 Mpa
ISO 527-2/17300 Mpa
Tensile strain断裂ISO 527-23.7 %
tensile strength断裂ISO 527-2160 Mpa
断裂ASTM D638157 Mpa
Wear factorWasherASTM D3702Modified80.0 10^-10in^5-min/ft-lb-hr
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/RF-1004FR BK
shrinkage rateMD:24小时ISO 294-40.47 %
MD：24小时ASTM D9550.50 %
TD：24hrASTM D9551.2 %
TD:24小时ISO 294-41.2 %
Water absorption rate24hr,50%RHASTM D5700.80 %