PC/ABS XCM840－BK1005 SABIC INNOVATIVE US
CYCOLAC™
Automotive interior parts,Electrical applications
High mobility,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/XCM840－BK1005 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 37 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 60.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| 23°C | ISO 180/1A | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCM840－BK1005 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 4300 Mpa | |
| tensile strength | 屈服 | ISO 527-2/5 | 56.0 Mpa |
| Tensile modulus | ASTM D638 | 4300 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 47.0 Mpa |
| elongation | 屈服 | ASTM D638 | 4.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 4.0 % |
| bending strength | ISO 178 | 100 Mpa | |
| Flexural modulus | ISO 178 | 4000 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 50 % |
| tensile strength | 断裂 | ASTM D638 | 47.0 Mpa |
| 屈服 | ASTM D638 | 56.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/XCM840－BK1005 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| TD：3.20mm | 内部方法 | 0.50-0.70 % | |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 12.7 cm3/10min |
| 260°C/5.0kg | ISO 1133 | 10.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/XCM840－BK1005 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.1E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 6.1E-05 cm/cm/°C | |
| vicat | ISO 306/B50 | 138 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 4.6E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 4.6E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 120 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 120 °C |