Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO GTX4610 1710 SABIC INNOVATIVE US
NORYL GTX™
Industrial machinery、Electrical applications
Hydrolysis resistance、High temperature resistan、Dimensional stability、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX4610 1710 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 12.0 J |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX4610 1710 |
|---|---|---|---|
| dielectric strength | 1.60mm,inOil | ASTM D149 | 24 KV/mm |
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| dielectric strength | 1.60mm,inAir | ASTM D149 | 23 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/GTX4610 1710 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 88.0 Mpa |
| 断裂 | ISO 527-2/5 | 88.0 Mpa | |
| bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 145 Mpa |
| tensile strength | 屈服4 | ASTM D638 | 88.0 Mpa |
| Tensile modulus | --3 | ASTM D638 | 5000 Mpa |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.0 % |
| Flexural modulus | 50.0mm跨距5 | ASTM D790 | 4600 Mpa |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.0 % |
| tensile strength | 断裂4 | ASTM D638 | 88.0 Mpa |
| bending strength | --6,7 | ISO 178 | 145 Mpa |
| Flexural modulus | --6 | ISO 178 | 4600 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 5000 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/GTX4610 1710 |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL 94 | 5VB5VA |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 825 °C |
| UL flame retardant rating | 0.8mm | UL 94 | V-1 |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/GTX4610 1710 |
|---|---|---|---|
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 15.0 cm3/10min |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 18 g/10min |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.88-0.94 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.50 % |
| 饱和,23°C | ISO 62 | 3.8 % | |
| Shrinkage rate | TD:3.20mm | 内部方法 | 0.95-1.0 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX4610 1710 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 220 °C |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7.4E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 220 °C |
| 0.45MPa,未退火,64.0mm跨距10，HDT | ISO 75-2/Bf | 224 °C | |
| vicat | -- | ASTMD152511 | 218 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 4.1E-05 cm/cm/°C |