Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC CGH2010KR MITSUBISHI ENGINEERING JAPAN
IUPILON™
Electronic and Electrical、Wrapping molding、Cable sheath、Wire and cable applicatio、pipeline、Soft handle、currency、Washer、Weatherproof sealing stri、Profile、Coating application、packing、Pipe fittings、Phone case、Fabric coating
Filler: Glass fiber reinf、10%、Filler by weight、Carbon fiber reinforced m
TDS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/CGH2010KR
Melt Volume-Flow Rate (MVR)
300°C/1.2kg
ISO1133
cm3/10min
3
Melt mass flow rate
300°C/1.2kg
ISO1133
g/10min
4
Mechanical performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/CGH2010KR
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
4
Tensile modulus
ISO527-2
Mpa
1
tensile strength
断裂
ISO527-2
Mpa
1
elongation
断裂
ISO527-2
%
1
Bending modulus
ISO178
Mpa
1
bending strength
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/CGH2010KR
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
5