Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC S-3000R MITSUBISHI GAS SHANGHAI
IUPILON™ 
Automotive sector、Electrical appliances
high strength、Weather resistance、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/S-3000R
Impact strength of simply supported beam without notch23°CISO179NoBreak
Charpy Notched Impact Strength23°CISO17967 kJ/m²
Mechanical propertiesTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/S-3000R
Nominal tensile fracture strainISO527-2120 %
Tensile stress屈服ISO527-262.0 Mpa
Tensile strain屈服ISO527-26.7 %
Bending stressISO17893.0 Mpa
Tensile modulusISO527-22400 Mpa
Flexural modulusISO1782300 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/S-3000R
Surface ResistivityIEC600936E+15 ohms
Relative Permittivity100HzIEC602503.10
Dissipation Factor1MHzIEC602509E-03
dielectric strength1.00mmIEC60243-131 KV/mm
Compared to the Leakage Tracking Index (CTI)CTIUL746PLC 2
Volume resistivityIEC600933E+16 ohms·cm
dielectric strength3.00mmIEC60243-118 KV/mm
Dissipation Factor100HzIEC602506E-04
Relative Permittivity1MHzIEC602503.10
physical property Test ConditionTest MethodMITSUBISHI GAS SHANGHAI/S-3000R
Shrinkage rateTD:3.20mm0.50to0.70 %
Water absorption rate饱和,23°CISO620.24 %
Melt volume flow rate300°C/1.2kgISO113314.0 cm3/10min
Shrinkage rateMD:3.20mm0.50to0.70 %
densityISO11831.20 g/cm³
melt mass-flow rate300°C/1.2kgISO113315 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/S-3000R
Heat Deflection Temperature0.45MPa,未退火ISO75-2/B139 °C
1.8MPa,未退火ISO75-2/A124 °C
Linear thermal expansion coefficientMDISO11359-26.5E-05 cm/cm/°C
TDISO11359-26.6E-05 cm/cm/°C