TPEE 5526 DUPONT LUXEMBOURG
BEXLOY® 
Automotive sector、Electrical field、Electronic field、Electrical appliances、Fitness equipment
Thermal stability、High mobility、UV resistance、Weather resistance、currency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT LUXEMBOURG/5526
Charpy Notched Impact Strength-30°C,局部断裂ISO 179/1eA150 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
23°CISO 179/1eUNoBreak
Charpy Notched Impact Strength23°CISO 179/1eANoBreak
-40°CISO 179/1eA30 kJ/m²
Impact strength of cantilever beam gap23°CISO 8256/1270 kJ/m²
hardnessTest ConditionTest MethodDUPONT LUXEMBOURG/5526
Shore hardness邵氏DISO 86855
邵氏D,15秒ISO 86851
Supplementary InformationTest ConditionTest MethodDUPONT LUXEMBOURG/5526
OdorVDA2705.00
Mechanical propertiesTest ConditionTest MethodDUPONT LUXEMBOURG/5526
Tensile modulusISO 527-2190 Mpa
tensile strength 10%应变ISO 527-211.0 Mpa
Tensile strain屈服ISO 527-235 %
Tensile creep modulus1000hrISO 899-1130 Mpa
wear resistanceISO 4649120 mm³
tensile strength 断裂ISO 527-240.0 Mpa
50%应变ISO 527-214.0 Mpa
Tensile creep modulus1hrISO 899-1170 Mpa
Nominal tensile fracture strainISO 527-2780 %
Tensile strain断裂ISO 527-2>300 %
Flexural modulusISO 178200 Mpa
tensile strength 屈服ISO 527-215.0 Mpa
5.0%应变ISO 527-26.90 Mpa
Electrical performanceTest ConditionTest MethodDUPONT LUXEMBOURG/5526
dielectric strengthIEC 60243-120 KV/mm
Volume resistivityIEC 600934E+13 ohms·cm
Dissipation Factor100HzIEC 602509E-03
relative permittivity100HzIEC 602504.90
1MHzIEC 602504.60
Surface ResistivityIEC 60093>1.0E+15 ohms
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
Dissipation Factor1MHzIEC 602500.038
flammabilityTest ConditionTest MethodDUPONT LUXEMBOURG/5526
UL flame retardant rating3.0mmIEC 60695-11-10,-20HB
Fogging-G-valuecondensateISO 64521E-04 g
UL flame retardant rating3.0mmUL 94HB
1.5mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302SE/B
Limiting Oxygen IndexISO 4589-221 %
UL flame retardant rating1.5mmUL 94HB
burning rate1.00mmISO 379528 mm/min
physical property Test ConditionTest MethodDUPONT LUXEMBOURG/5526
Shrinkage rateTDISO 294-41.4 %
MDISO 294-41.4 %
Water absorption rate饱和,23°C,2.00mmISO 620.60 %
melt mass-flow rateISO 113318 g/10min
Water absorption rate23°C,24hrISO 620.60 %
MediumDensity1.04 g/cm³
Melt volume flow rate220°C/2.16kgISO 113317.5 cm3/10min
densityISO 11831.19 g/cm³
SpecificHeatCapacity of Melt2110 J/kg/°C
ThermalConductivityofMelt0.19 W/m/K
Water absorption rate平衡,23°C,2.00mm,50%RHISO 620.20 %
elastomerTest ConditionTest MethodDUPONT LUXEMBOURG/5526
tear strength流量ISO 34-1130 kN/m
横向流量ISO 34-1130 kN/m
Thermal performanceTest ConditionTest MethodDUPONT LUXEMBOURG/5526
melting temperatureISO 11357-3203 °C
Linear coefficient of thermal expansionTD：--ISO 11359-22E-04 cm/cm/°C
MD：-40to23°CISO 11359-21.8E-04 cm/cm/°C
TD：-40to23°CISO 11359-21.7E-04 cm/cm/°C
MD：--ISO 11359-22E-04 cm/cm/°C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B65.0 °C
brittle temperatureISO 974-98.0 °C
vicat--ISO 306/A50180 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A45.0 °C
vicat--ISO 306/B5075.0 °C
Linear coefficient of thermal expansionTD：EffectiveThermalDiffusivityISO 11359-29E-08 m²/s
Glass Transition TemperatureISO 11357-2-20.0 °C