Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA/MXD6 1524-9008 SOLVAY USA
IXEF®
Shell、Phone
Filler: Glass fiber reinf、50% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/1524-9008 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 48 kJ/m² |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/1524-9008 |
|---|---|---|---|
| Hot wire ignition (HWI) | 3.00mm | UL 746 | sec |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | UL 746 | V |
| Hot wire ignition (HWI) | 1.50mm | UL 746 | sec |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 0.40mm | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | 0.400mm | UL 746 | sec |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | 0.750mm | UL 746 | sec |
| High arc combustion index (HAI) | 0.400mm | UL 746 | |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 1 |
| 0.75mm | UL 746 | PLC 2 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| High Voltage Arc Traceability Rate (HVTR) | 3.00mm | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 3.00mm | UL 746 | |
| dielectric constant | 2.40GHz | ASTM D2520 | 4.44 |
| Hot wire ignition (HWI) | 0.40mm | UL 746 | PLC 1 |
| High arc combustion index (HAI) | 0.750mm | UL 746 | |
| Hot wire ignition (HWI) | 0.75mm | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 1.50mm | UL 746 | |
| Dissipation Factor | 2.40GHz | ASTM D2520 | 0.012 |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/1524-9008 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 20000 Mpa | |
| bending strength | ISO 178 | 330 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.9 % |
| Flexural modulus | ISO 178 | 18500 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 230 Mpa |
| flammability | Test Condition | Test Method | SOLVAY USA/1524-9008 |
|---|---|---|---|
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 850 °C |
| 1.5mm | IEC 60695-2-13 | 825 °C | |
| 0.40mm | IEC 60695-2-13 | 775 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 37 % | |
| UL flame retardant rating | 0.40mm | UL 94 | V-0 |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 800 °C |
| physical property | Test Condition | Test Method | SOLVAY USA/1524-9008 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.10-0.30 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.30 % |
| Equilibrium,65%RH | 内部方法 | 1.3 % | |
| 平衡,50%RH | 内部方法 | 1.0 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/1524-9008 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 227 °C |