Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DCP32-NCLT SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™
Automotive components,Sports equipment,Electronic and electrical components
High mobility,wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DCP32-NCLT |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 440 J/m |
| 23°C3 | ISO 180/1U | 28 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DCP32-NCLT |
|---|---|---|---|
| Tensile modulus | --1 | ASTM D638 | 7580 Mpa |
| elongation | 屈服 | ASTM D638 | 2.1 % |
| tensile strength | 断裂 | ASTM D638 | 91.0 Mpa |
| 断裂 | ISO 527-2 | 93.0 Mpa | |
| Flexural modulus | -- | ISO 178 | 6700 Mpa |
| bending strength | -- | ISO 178 | 142 Mpa |
| coefficient of friction | Dynamic | ASTM D3702 | 0.35 |
| elongation | 断裂 | ASTM D638 | 2.1 % |
| bending strength | -- | ASTM D790 | 137 Mpa |
| tensile strength | 屈服 | ASTM D638 | 91.0 Mpa |
| 屈服 | ISO 527-2 | 93.0 Mpa | |
| coefficient of friction | Static | ASTM D3702 | 0.36 |
| Tensile modulus | -- | ISO 527-2/1 | 7470 Mpa |
| Flexural modulus | -- | ASTM D790 | 6200 Mpa |
| Wear factor | ASTM D3702 | 9.9E+6 10^-8 mm³/N·m |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DCP32-NCLT |
|---|---|---|---|
| Shrinkage rate | 流动 : 24小时 | ASTM D955 | 0.30 - 0.50 % |
| 流量 : 24小时 | ISO 294-4 | 0.43 % | |
| 横向流量 : 24小时 | ISO 294-4 | 0.54 % | |
| density | ASTM D792 | 1.30 g/cm³ | |
| Shrinkage rate | 横向流动 : 24小时 | ASTM D955 | 0.40 - 0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DCP32-NCLT |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 4.1E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 6.3E-5 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 6.3E-5 cm/cm/°C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DCP32-NCLT |
|---|---|---|---|
| drying time | 4.0 hr | ||
| screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Back pressure | 0.200 to 0.300 Mpa |