Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HN-3104-K2495 Samsung Cheil South Korea
INFINO®
smart meter 、Wiring equipment
Glass fiber reinforced、Flame retardant、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/HN-3104-K2495 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/HN-3104-K2495 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 115 |
| R级 | ASTM D785 | 115 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/HN-3104-K2495 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 60.0 Mpa |
| Tensile modulus | ASTM D638 | 3400 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 60.0 Mpa |
| elongation | 断裂 | ASTM D638 | 6.0 % |
| bending strength | ISO 178 | 90.0 Mpa | |
| Flexural modulus | ISO 178 | 3500 Mpa | |
| bending strength | ASTM D790 | 98.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 6.0 % |
| Tensile modulus | ISO 527-2/5 | 3500 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 54.0 Mpa |
| 屈服 | ASTM D638 | 54.0 Mpa | |
| Flexural modulus | ASTM D790 | 3400 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/HN-3104-K2495 |
|---|---|---|---|
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/HN-3104-K2495 |
|---|---|---|---|
| ash content | -- | ASTM D5630 | 11 % |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.10-0.20 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 8.0 g/10min |
| Shrinkage rate | TD:3.20mm | ISO 2577 | 0.10-0.20 % |
| ash content | -- | ISO 3451 | 11 % |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 8.0 g/10min |
| Shrinkage rate | TD：3.20mm | ASTM D955 | 0.10-0.20 % |
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 13 g/10min |
| 250°C/10.0kg | ISO 1133 | 13 g/10min | |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.10-0.20 % |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/HN-3104-K2495 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 137 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 140 °C | |
| 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 136 °C | |
| vicat | ISO 306/B50 | 136135 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 139 °C |