ASA XTWM206-BK1C091 SABIC INNOVATIVE US

GELOY™

Electronic and electrical components,Lawn garden equipment,High temperature applications

Colorable,Weather resistance

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE US/XTWM206-BK1C091
Rockwell hardness	R-Scale	ASTM D785	100

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/XTWM206-BK1C091
Ball Pressure Test	83 to 87°C	IEC 60695-10-2	通过
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	97.0 °C
		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	84.0 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span11	ISO 75-2/Af	84.0 °C
		0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span11	ISO 75-2/Bf	98.0 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	8.3E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	9.4E-5 cm/cm/°C
		Across Flow : -40°C	ISO 11359-2	9.4E-5 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	8.4E-5 cm/cm/°C
Vicat softening temperature	--		98.0 °C
		--	ISO 306/B120	99.0 °C
		--	ISO 306/B50	95.0 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/XTWM206-BK1C091
Bending modulus	--8	ISO 178	2380 Mpa
Bending modulus		50.0 mm Span7	ASTM D790	2450 Mpa
bending strength	--8,9	ISO 178	64.0 Mpa
bending strength		Yield, 50.0 mm Span7	ASTM D790	74.0 Mpa
elongation	Yield	ISO 527-2/50	2.8 %
		Yield6	ASTM D638	2.5 %
		Yield5	ASTM D638	2.7 %
		Break5	ASTM D638	26 %
		Break6	ASTM D638	27 %
		Break	ISO 527-2/50	36 %
Tensile modulus	--4	ASTM D638	2400 Mpa
		--3	ASTM D638	2360 Mpa
		--	ISO 527-2/1	2350 Mpa
tensile strength	Yield	ISO 527-2/50	45.0 Mpa
		Break	ISO 527-2/50	36.0 Mpa
		Break5	ASTM D638	37.0 Mpa
		Break6	ASTM D638	36.0 Mpa
		Yield6	ASTM D638	43.0 Mpa
		Yield5	ASTM D638	46.0 Mpa

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/XTWM206-BK1C091
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	7.1 g/10 min
		220°C/10.0 kg	ASTM D1238	8.8 g/10 min
		280°C/3.8 kg	ASTM D1238	7.2 g/10 min
Melt Volume Flow Rate (MVR)	260°C/5.0 kg	ISO 1133	9.00 cm3/10min
Outdoor applicability		UL 746C	f1
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.75 %
		Flow : 3.20 mm	Internal Method	0.40 - 0.70 %
		Flow 2	Internal Method	0.40 - 0.70 %
Water absorption rate	Saturation, 23°C	ISO 62	0.50 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.20 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/XTWM206-BK1C091
Dart impact	-30°C, Total Energy	ASTM D3763	3.00 J
Dart impact		23°C, Total Energy	ASTM D3763	36.0 J

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/XTWM206-BK1C091
UL flame retardant rating	1.5 mm	UL 94	HB

injection	Test Condition	Test Method	SABIC INNOVATIVE US/XTWM206-BK1C091
Back pressure			0.300 to 1.00 Mpa
drying temperature			85 to 90 °C
drying time			4.0 hr
Exhaust hole depth			0.038 to 0.076 mm
Mold temperature			60 to 85 °C
Processing (melt) temperature			240 to 270 °C
Screw speed			30 to 80 rpm
Spray nozzle temperature			220 to 255 °C
Suggested injection volume			40 to 80 %
Suggested maximum moisture content			0.040 %
Temperature at the front of the material cylinder			230 to 260 °C
Temperature at the rear of the barrel			215 to 250 °C
Temperature in the middle of the barrel			220 to 255 °C

optical performance	Test Condition	Test Method	SABIC INNOVATIVE US/XTWM206-BK1C091
gloss	60°, 无织构	ASTM D523	93