Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 2000-3 CELANESE USA
--
Electrical applications,Automotive Applications,currency
High toughness,Hydrolysis resistance,Thermal stability,UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodCELANESE USA/2000-3
Charpy Notched Impact Strength23°CISO 179/1eA4.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU100 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A3.2 kJ/m²
hardnessTest ConditionTest MethodCELANESE USA/2000-3
Rockwell hardnessM计秤ISO 2039-278
Mechanical propertiesTest ConditionTest MethodCELANESE USA/2000-3
Fracture, 23 ° CASTM D63855.8 Mpa
Tensile strain屈服ISO 527-2/1A/504.0 %
断裂ISO 527-2/1A/5030 %
Tensile modulusISO 527-2/1A/12700 Mpa
bending strength23°CISO 17885.0 Mpa
Surrender, 23 ° CASTM D63857.2 Mpa
Flexural modulus23°CISO 1782600 Mpa
yieldISO 527-2/1A/5060.0 Mpa
Electrical performanceTest ConditionTest MethodCELANESE USA/2000-3
Compared to the Leakage Tracking Index (CTI)ASTM D3638PLC 0
--1ASTM D14917 KV/mm
relative permittivity1MHzIEC 602503.20
flammabilityTest ConditionTest MethodCELANESE USA/2000-3
UL flame retardant ratingUL 94HB
physical property Test ConditionTest MethodCELANESE USA/2000-3
Shrinkage rateMDASTM D9551.8-2.0 %
densityASTM D7921.31 g/cm³
Thermal performanceTest ConditionTest MethodCELANESE USA/2000-3
1.8MPa, Not annealedISO 75-2/A55.0 °C
0.45MPa, Not annealedISO 75-2/B155 °C